合成了一种新的四硫富瓦烯衍生物修饰的银溶胶,并通过透射电子显微镜、红外、紫外、拉曼光谱和循环伏安法测试技术对其进行了表征. 透射电子显微镜照片显示,纳米银颗粒为球形,其直径约为70 nm,用四硫富瓦烯衍生物修饰的银纳米粒子有较好的单分散性. 将修饰后的银溶胶固着在Pt片电极上进行了电化学测定. 结果显示,修饰后的纳米银颗粒具有较好的氧化还原活性. 2组氧化-还原峰(E1/2)为0.67和0.86 V,分别对应于TTF/TTF·+和TTF·+/TTF2+ 2个单电子氧化过程.
参考文献
| [1] | Pergolese B,Muniz-Miranda M,Bigotto A.J Phys Chem B[J],2004,108:5 698 |
| [2] | Erwin G.Anal Chem[J],1985,57:1 658 |
| [3] | Tan Y W,Jiang L,Li Y F,et al.J Phys Chem B[J],2002,106:3 131 |
| [4] | Jasmina H,Nada M D,Gregory A W,et al.J Am Chem Soc[J],2002,124:4 536 |
| [5] | Marek P,Blanka V,Josef S,et al.Langmuir[J],2005,21:2 956 |
| [6] | Talley C E,Jusinski L,Hollars C W,et al.Anal Chem[J],2004,76:7 064 |
| [7] | McFarland A D,Van Duyne R P.Nano Lett[J],2003,3:1 057 |
| [8] | Hutter E,Fendler J H,Roy D.J Phys Chem B[J],2001,105:11 159 |
| [9] | Coronado E, mez-García C G.J Chem Rev[J],1998,98:273 |
| [10] | Williams J M,Beno M A,Wang H H,et al.Acc Chem Res[J],1985,18:261 |
| [11] | Segura J L,Martin N.Angew Chem Int Ed[J],2001,40:1 372 |
| [12] | Nielsen M B,Lomholt M C,Becher J.Chem Soc Rev[J],2000,29:153 |
| [13] | Najai H,Yoshihara M,Fujihara H.Langmuir[J],1999,15:8 574 |
| [14] | Dai J,Guo L,Yun J,et al.J Nanosci Nanotech[J],2005,5:474 |
| [15] | Jia C Y,Zhang D Q,Xu W,et al.Organ Lett[J],2001,3(12):1 941 |
| [16] | Lee P C,Meisel D.J Phys Chem[J],1982,86:3 391 |
| [17] | Brown K R,Walter D G,Natan M.J Chem Mater[J],2000,12:306 |
| [18] | Moor A J,Goldenberg L M,Bryce M R,et al.J Org Chem[J],2000,65:8 269 |
| [19] | Liu S G,Liu H,Bandyopadhyay K,et al.J Org Chem[J],2000,65:3 292 |
| [20] | Moore A J,Goldenberg L M,Bryce M R,et al.Adv Mater[J],1998,10:395 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%