用4,4'-二氨基二苯基甲烷(DDM), 3,3'-二羟基联苯胺(HAB),与均苯四甲酸二酐(PMDA)在N,N-二甲基乙酰胺中室温缩聚,制备了3种共聚酰胺酸(CPAA);CPAA膜经热处理失水环化,形成共聚酰亚胺(CPI);在N2气下经500 ℃热处理,重排转变为DDM-PMDA-HAB(噁)唑酰亚胺共聚物(CPBI). ATR光谱显示了CPI 和CPBI膜的特征结构. TGA分析佐证了(噁)唑化转变. CPBI膜均显示优良的耐热性(用质量损失5%时的温度Td表示),比相应的CPI高93～138 ℃;比二元聚合物PMDA-HAB聚苯并(噁)唑(PBO)高65～86 ℃. 廉价的DDM在二胺单体中所占摩尔分数为75%时,CPBI仍保持优良的耐热性(Td为573 ℃).
参考文献
| [1] | JIN Ning-Ren(金宁人),HUANG Yin-Hua(黄银华),WANG Xue-Jie(王学杰).J Zhejiang Univ Tech(浙江工业大学学报)[J],2003,31(1):82 |
| [2] | Hasegawa M,Kobayashi J,Vladimirov L.J Photopolymer Sci Tech[J],2004,17(2):253 |
| [3] | XIA Yan-Zhi(夏延致),QI Ming-Zheng(綦名正),JI Quan(纪全),et al.J Qingdao Univ(青岛大学化学学报)[J],2002,15(4):21 |
| [4] | Park K H,Song S,Lee Y S,et al.Polym J[J],1998,30(6):470 |
| [5] | Ueda M,Ebara K,Shibasaki Y.J Photopolymer Sci Tech[J],2003,16(2):237 |
| [6] | Tullos G L,Mathias L J.Polymer[J],1999,(40):3 463 |
| [7] | Hsiao S-H,Huang Y-H.Eur Polym J[J],2004,40(6):1 127 |
| [8] | HAN Zhe-Wen(韩哲文),LU Zhi-Bao(陆志豹),SHI Xiao-Yang(石晓阳),et al.Acta Polym Sin(高分子学报)[J],1997,(2):141 |
| [9] | ZHANG Chun-Yan(张春燕),SHI Zi-Xing(史子兴),ZHU Zi-Kang(朱子康),et al.Chem J Chinese Univ(高等学校化学学报)[J],2004,25(3):556 |
| [10] | LI Jin-Huan(李金焕),HUANG Yu-Dong(黄玉东),XU Hui(许辉).Polym Mater Sci Eng(高分子材料科学与工程)[J],2003,19(6):46 |
| [11] | Fukukawa K,Shibasaki Y,Ueda M.Macromolecules[J],2004,37(22):8 256 |
| [12] | Fukukawa K-I,Shibasaki Y,Ueda M.Polymer J[J],2004,36(6):489 |
| [13] | Tullos G L,Powers J M,Jeskey S J,et al.Macromolecules[J],1999,32(11):3 598 |
| [14] | KE Yi-Kan(柯以侃)Chief-Edr(主编).Handbook of Analytical Chemistry(分析化学手册)[M],Third Portion(第3分册),Spectroscopic Analysis9(光谱分析).Beijing(北京):Chemical Industry Press(化学工业出版社),1998 |
| [15] | Guzman-Lucero D,Likhatchev D.Polymer Bull[J],2002,48(3):261 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%