以4-甲基溴苯与苯硼酸的偶联为探针反应,在常规条件下研究了单膦和双齿膦二茂铁衍生物作为钯催化剂配体对Suzuki-Miyaura偶联反应的催化规律.结果表明,在所研究的配体中,PPFOMe(1-[2-(二苯基膦)二茂铁基]乙基甲基醚)与钯配位所得催化剂对该探针反应具有较好的催化活性.对于该溴代苯类与苯硼酸的Suzuki-Miyaura偶联反应体系,K2CO3比CsF促进效果更好,Pd(OAc)2比PdCl2催化效果更好.使用K2CO3作为促进剂,在110℃反应1 h即可达到94%收率.在同一条件下对多种取代溴苯与苯硼酸反应均可得到90%以上产物收率的结果表明,该二茂铁基膦衍生物作为钯的配合物对于Suzuki-Miyaura偶联反应有很好的催化作用.
参考文献
[1] | Miyaura N,Yanagi T,Suzuki A.Synth Commun[J],1981,11:513 |
[2] | Suzuki A.J Organomet Chem[J],1999,576:147 |
[3] | Stanforth S P.Tetrahedron[J],1998,54:263 |
[4] | Littke A F,Fu G C.Angew Chem Int Ed[J],2002,41:4 176 |
[5] | Nájera C,Gil-Moltó J,Karlstr(o)m S.Adv Synth Catal[J],2004,346:1 798 |
[6] | CHENG Ge(程格),TAO Quan-Hua (陶全华),YANG Qiong-Hui (杨琼辉),WANG Yue-Chuan (王跃川).Chinese J Org Chem(有机化学)[J],2000,20:874 |
[7] | ZHOU Shao-Lin(周少林),XU Li-Wen (徐利文),XIA Chun-Gu (夏春谷),LI Jing-Wei (李经纬),LI Fu-Wei (李福伟).Chinese J Org Chem(有机化学)[J],2004,24:1 501 |
[8] | Hamada T,Chieffi A,Ahman J,Buchwald S L.J Am Chem Soc[J],2002,124:1 261 |
[9] | Parrish C A,Buchwald S L.J Org Chem[J],2001,66:3 820 |
[10] | Jensen J F,Johannsen M.Org Lett[J],2003,5:3 025 |
[11] | Tang Z Y,Lu Y,Hu Q S.Org Lett[J],2003,5:297 |
[12] | Baillie C,Zhang L X,Xiao J L.J Org Chem[J],2004,69:7 779 |
[13] | Colacot T J,Shea H A.Org Lett[J],2004,6:3 731 |
[14] | Hayashi T,Mise T,Fukushima M,Kagotani M,Nagashima N,Hamada Y,Matasumoto A,Kauakami S,Konishi M,Yamamoto K,Kumada M.Bull Chem Soc Jpn[J],1980,53:1 138 |
[15] | Cammidge A N,Crepy K V L.Chem Commun[J],2000:1 723 |
[16] | Wright S W,Hageman D L,McClure L D.J Org Chem[J],1994,59:6 095 |
[17] | Miyaura N,Suzuki A.Chem Rev[J],1995,95:2 457 |
[18] | Satoh T,Kawamura Y,Miura M,Nomura M.Angew Chem Int Ed[J],1997,36:1 740 |
[19] | Marcoux J F,Wagaw S,Buchwald S L.J Org Chem[J],1997,62:1 568 |
[20] | Walker S D,Barder T E,Martinelli J R,Buchwald S L.Angew Chem Int Ed[J],2004,43:1 871 |
[21] | Kataoka N,Shelby Q,Stambuli J P,Hartwig J F.J Org Chem[J],2002,67:5 553 |
[22] | Littke A F,Fu G C.Angew Chem Int Ed[J],1998,37:3 387 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%