合成了环氧树脂新型有机硅改性剂3,3',3″,-三羟基苯氧基硅烷三缩水甘油醚,用加热红外光谱及差热扫描(DSC)测试技术研究了其反应活性及改性双酚F环氧树脂的固化特性,测试了固化物的性能.结果表明,有机硅的反应速率低于双酚F环氧树脂;2,4-咪唑质量分数为2%时,有机硅的固化温度范围较双酚F环氧树脂降低约20℃.Kissinger法计算改性双酚F环氧树脂的固化反应活化能为50.53 kJ/mol,低于未改性树脂(66.68 kJ/mol),频率因子对数值为9.783,低于未改性树脂(16.379),反应速率常数低于未改性树脂.合成的改性剂可使双酚F环氧树脂固化物的拉伸强度、弯曲强度分别提高10.4%及53.6%,线性热膨胀系数降低18.8%,抗开裂指数提高52.2%,同时保持固化物较高的玻璃化温度.
参考文献
| [1] | Zhou Z F,Zhao F.Thermosetting Resin[J],1998,2:12 |
| [2] | Bai Z W,Zhang Q H.J Funct Polym[J],1996,9(3):437 |
| [3] | Alagar M,Ashok Kunar A,Mahash K P.Eur Polym J[J],2000,36:2 449 |
| [4] | Hsiue G H.Polym Degradation and Stability[J],2001,73(2):309 |
| [5] | Zhang B,Liu X L,Huang Y.J Funct Polym[J],2000,13(1):69 |
| [6] | Emel Y,Iskender Y.Polymer[J],1998,39(8 -9):1 691 |
| [7] | Lin S T,Huang S K.J Appl Polym Sci[J],1996,62(10):1 641 |
| [8] | Chen P,Liu L Z.Acts,Polym Sin[J],1994,(6):641 |
| [9] | Zhou T L,Gu M Y,Jin Y P,Wang J X.Polymer[J],2005,46:6 174 |
| [10] | Sun G,Sun H G,Liu Y,Zhao B Y,Zhu N,Hu K A.Polymer[J],2007,48:330 |
| [11] | Pan P J,Shan G R,Huang Z M,Yu Z X.Acta Polym Sin[J],2006,(1):21 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%