通过溶胶-凝胶法(sol-gel),以钛酸四异丙酯和Tb2O3为前驱体制备出一系列不同掺铽量的TiO2柱撑膨润土(Tb-TiO2-PILCs). 采用XRD、BET测试技术对制得的复合催化剂进行了表征. 并以五氯酚钠为目标污染物,考察了它们的光催化性能. 结果表明,掺铽与未掺铽的Ti02-PILCs中TiO2主要以锐钛矿型存在;掺铽的Tb-TiO2-PILCs的光催化活性明显优于未掺铽的TiO2-PILC,Tb/Ti质量比为0.5%的Tb-TiO2-PILC 催化活性最佳. 复合催化剂具有回收容易,重复使用性好等特点.
参考文献
| [1] | Hoffmann M R,Martin S T,Choi W,Bahnemann D W.Chem Rev[J],1995,95:69 |
| [2] | Fujishima A,Tat N R,Donald A T.J Photochem Photobio C:Photochem Rev[J],2000,1:1 |
| [3] | Liu G,Wu T,Zhao J,Horikoshi S,Hidaka H.Environ Sci Tech[J],1999,33:2 081 |
| [4] | ZHENG Shan(郑珊),GAO Lian(高濂),GUO Jing-Kun(郭景坤).Chem J Chinese Univ(高等学校化学学报)[J],2002,23(6):1 129 |
| [5] | Sakthivel S,Shankar M V,Palanichamy M.Water Res[J],2004,38:3 001 |
| [6] | FU Hong-Gang(付宏刚),WANG Jian-Qiang(王建强),REN Zhi-Yu(任志宇),YAN Peng-Fei(闫鹏飞),YU Hai-Tao(于海涛),XIN Bai-Fu(辛柏福),YUAN Fu-Long(袁福龙).Chem J Chinese Univ(高等学校化学学报)[J],2003,24(9):1 671 |
| [7] | ZHANG Hua-Xing(张华星),ZHANG Yu-Hong(张玉红),XU Yong-Xi(徐永熙),WANG Yan-Guang(王彦广).Acta Chim Sinica(化学学报)[J],2003,61(11):1 813 |
| [8] | Ranjit K T,Willner I,Bossmann S H,Braun A M.Environ Sci Tech[J],2001,35:1 544 |
| [9] | Arana J,Dona-Rodriguez J M,Rendon E T.Appl Catal B:Environ[J],2003,44:153 |
| [10] | Lee D K,Kim S C,Kim S J.Chem Eng J[J],2004,102:93 |
| [11] | Bhattacharyya A,Kawi S,Ray M B.Catal Today[J],2004,58:431 |
| [12] | Lim T H,Kim S D.Chem Eng Process[J],2005,44:327 |
| [13] | Ding Z,Zhu H Y,Greenfield P F,Lu G Q.J Colloid Interface Sci[J],2001,238:267 |
| [14] | Shimizu K,Kaneko T,Fujishima T,Kodama T,Yoshida H,Kitayama Y.Appl Catal A:Gen[J],2002,225:185 |
| [15] | OoKa C,Yoshida H,Suzuki K,Hattori T.Micropor Mesopor Mater[J],2004,67:143 |
| [16] | Arfaoui J,Boudali L K,Ghorbel A.Catal Commun[J],2006,7:86 |
| [17] | Xu A W,Gao Y,Liu H Q.J Catal[J],2002,207:151 |
| [18] | Wang Y Q,Cheng H M,Zhang L.J Mol Catal A:Chem[J],2000,151:205 |
| [19] | EI-Maazawi M,Finken A N,Nair A B,Grassian V H.J Catal[J],2000,191:138 |
| [20] | Matthews R W.J Catal[J],1988,113:549 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%