在酸性条件下,以导电玻璃(ITO)为基底合成sBA.16分子筛膜.所制备的SBA-16薄膜孔径均匀,具有体心立方结构(属于Im3m空间群).在由CdCl2和Na2S2O3组成的电解液中,调节pH值为2～3.利用直流恒电位电沉积法,调节电位为-0.7 V,沉积时间为50 min,在SBA-16膜/ITO电极表面电沉积生长出"花状"CdS纳米晶体,利用SEM、TEM等技术研究了CdS纳米晶体形貌和结构,同时进行了荧光光谱测试.结果表明,电沉积合成的CdS生长在电极表面而不是生长在介孔孔道中.并能够产生荧光谱峰.
参考文献
| [1] | Hillhouse H W,Egmond J W,Tsapatsis M.Langmuir[J],1999,15(13):4 544 |
| [2] | Miyata H,Kuroda K.Adv Mater[J],1999,11(17):1 448 |
| [3] | Miyata H,Kuroda K.Chem Mater[J],2000,12(1):49 |
| [4] | Yuliarto B,Zhou H S,Yamada T,Honm A I,Asai K.Chem Phys Chem[J],2004,5(2):261 |
| [5] | Yamada T,Zhou H S,Uchida H,Tomita M,Ueno Y,Honma I,Asai K,Katsube T.Micro Meso Mater[J],2002,54(3):269 |
| [6] | Yamada T,Zhou H S,Uchida H,Tomita M,Katsube T.Adv Mater[J],2002,14(11):812 |
| [7] | Morey M S,O'Brien S,Schwarz S,Stucky G D.Chem Mater[J],2000,12(4):898 |
| [8] | Aguilera A,Jayaraman V,Sanagapalli S,Singh R S,Jayaraman V,Sampson K,Singh V P.So Energy Mater Sol Cells[J],2006,90(6):713 |
| [9] | Premaratne K,Akuranthilaka S N,Dharmadasa I M,Samantilleka A P.Renew Energy[J],2003,29(4):549 |
| [10] | Huo Q S,Zhao D Y,Feng J L,Weston K,Buratto S K,Stucky G D,Schacht S,Schuth F.Adv Mater[J],1997,9(12):974 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%