将纳米SiO2改性并与异佛尔酮二异氰酸酯、聚酯二元醇、二羟甲基丙酸在月桂酸丁基锡催化下经原位聚合制备出水性聚氨酯纳米SiO2复合材料. 用DSC、TG、TEM及动态力学分析等测试技术研究了纳米SiO2的成分对水性聚氨酯的形态、性能的影响. 结果表明,质量分数在3.0%以下时,SiO2均匀地分散在水性聚氨酯中,高于3.0%时有少量聚集;SiO2的加入使水性聚氨酯复合材料软段与硬段微相分离明显,玻璃化转变温度的范围加宽,热分解温度比未加入的高50 ℃以上. 此外,加入质量分数为0.5%SiO2时,断裂伸长率由550%降至430%,吸水率由16.8%降至4.5%,拉伸强度由3.4 MPa增至5.95 MPa. 当加入质量分数为2.5%SiO2时,断裂伸长率降至210%,吸水率降至2.3%,拉伸强度增至7.58 MPa.
参考文献
| [1] | Takanashi H,Muramatsu I,Motomura M.EP 1 209 180A1[P],2002:14. |
| [2] | Wicks Z W,Wicks D A,Rosthauser J W.Prog Org Coatings[J],2002,44(2):161 |
| [3] | Wang L F,Ji Q,Glass T E,Ward T C,McGrath J E,Muggli M,Burns G,Sorathia U.Polymer[J],2000,41:5 083 |
| [4] | Tan H,Xie X Y,Li J H,Zhong Y P,Fu Q.Polymer[J],2004,45:1 495 |
| [5] | Benrashid R,Nelson G L,Linn J H,Hanley K H,Wade W R.J Appl Polym Sci[J],1993,49:523 |
| [6] | WANG Chun-Yan(王春艳),ZHU Chuan-Fang(朱传方),WAN Ting(万婷),CHEN Jing-Jing(陈晶晶).Chinese J Appl Chem(应用化学)[J],2006,23(4):441 |
| [7] | Biswas M,Sinha Ray S.Adv Polym Sci[J],2001,155:167 |
| [8] | Giannelis E P.Appl Organomet Chem[J],1998,12:675 |
| [9] | Xu R,Manias E,Snyder A J,Runt J.Macromolecules[J],2001,34:337 |
| [10] | Bharadwaj R K.Macro-molecules[J],2001,34:1 989 |
| [11] | Kim Byung K,Jang W S,Han M J.European Polym J[J],2003,39:85 |
| [12] | Kwon J Y,Kim H D.J Appl Polym Sci[J],2005,96:595 |
| [13] | Mamunya Ye P,Shtompel V I,Lebedev E V,Pissis P,Kanapitsas A,Boiteux G.European Polym J[J],2004,40:2 323 |
| [14] | Chen Y C,Zhou S X,Yang H H,Gu G X,Wu L M.J Colloid and Interface Sci[J],2004,279:370 |
| [15] | Kuan H C,Chuang W P,Ma C C.J Mater Sci[J],2005,40:179 |
| [16] | Jesionowski T,Krysztafkiewicz A.Colloids Surf A Physicochem[J],2002,207:49 |
| [17] | Kuan H C,Su H Y,Ma C C M.J Mater Sci[J],2005,40:6 063 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%