采用接枝有聚电解质--季铵化聚乙烯亚胺的硅胶微粒,吸附去除水介质中的铬酸根阴离子. 通过γ-氯丙基三甲氧基硅烷的偶联,将聚乙烯亚胺(PEI)偶合接枝在微米级硅胶微粒表面,制得PEI/SiO2. 采用叔胺化与季铵化反应,将接枝微粒PEI/SiO2表面的PEI大分子链季铵化,制备了在硅胶表面接枝有季铵化聚乙烯亚胺的功能微粒QPEI/SiO2. 用红外光谱测试技术对其化学结构进行了表征,测定了该微粒的Zeta电位. 采用静态法研究了QPEI/SiO2对铬酸根的吸附性能. 结果表明,凭借强烈的静电相互作用,QPEI/SiO2对铬酸根阴离子可产生很强的吸附作用,饱和吸附量达0.14 g/g. 等温吸附满足Langmuir吸附等温方程. 影响QPEI/SiO2吸附性能的主要因素是接枝微粒QPEI/SiO2的季铵化程度,季铵化程度越高,吸附容量越大. 介质的pH值对吸附作用影响很小.
参考文献
| [1] | Atia A A.J Hazardous Mater B[J],2006,137:1 049 |
| [2] | Kumar P A,Ray M,Chakraborty S.J Hazardous Mater[J],2007,143:24 |
| [3] | Benhammou A,Yaacoubi A,Lahbib N,Tanouti B.J Hazardous Mater[J],2007,140:104 |
| [4] | Dermou E,Velissariou A,Xenos D,Vayenas D V.J Hazardous Mater[J],2005,B126:78 |
| [5] | Kabaya N,Arda M,Trochimczukc A,Streat M.Reactive and Func Polym[J],2004,59:9 |
| [6] | Wang K Y,Chung T-Sh.J Membrane Sci[J],2006,281:307 |
| [7] | Zouboulis A I,Loukidou M X,Matis K A.Process Biochem[J],2004,39:909 |
| [8] | Bowman R S.Microporous and Mesoporous Mater[J],2003,61:43 |
| [9] | Amara M,Kerdjoudj H.Talanta[J],2003,60:991 |
| [10] | Uysal M,Ar I.J Hazardous Mater[J],2007,149(2):482 |
| [11] | Maryuk O,Pikus S,Olszewska E,Majdan M,Skrzypek H,Ziba E.Mater Lett[J],2005,59:2 015 |
| [12] | Gao B J,Jiang P F,Lei H B.Mater Lett[J],2006,60:3 398 |
| [13] | Gao B J,Zhang X,Zhu Y.J Biomater Sci-polym Edn[J],2007,18:531 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%