采用固相低热合成法制备了纳米草酸钴,在不同条件下将聚苯胺原位生长在草酸钴表面获得兼具导电性和导磁性的聚苯胺/CoC_2 O_4纳米复合物. 考察了反应物配比、混合条件、活性剂的种类和用量对产物形貌结构及其电磁性质的影响. 通过透射电子显微镜、X射线衍射、热重分析等测试技术表征了合成产物. 结果表明,通过改变纳米CoC_2 O_4与聚苯胺原位生长的复合条件可以有效调控产物的形貌结构及其微波吸收性能. 最佳实验结果为:在超声作用下获得的聚苯胺/CoC_2 O_4试样在8.6 GHz 处具有最大的反射损耗(-28.8 dB),大于-10 dB的带宽达3.2 GHz.
Polyaniline/CoC_2 O_4 nanocomposite with both electrical and magnetic conductivities was synthesized by means of in-situ growth of polyaniline under different conditions on the surface of nano-cobalt oxalate, which was obtained by low heating solid state reaction. The influences of different reaction conditions including reactants' ratio, mixing methods, type and quantity of surfactants on the morphology and structure and their electromagnetic properties of resulting composites were investigated. The products were characterized by TEM, XRD, and TG analysis techniques. The results indicate that the morphology and structure and their microwave absorbing performance of the as-prepared nanocomposites can be effectively tuned by changing the in-situ complex conditions. The optimal experimental results were as follows: polyaniline/CoC_2 O_4 nanocomposite obtained under ultrasonication showed a maximum reflection loss of -28. 8 dB at 8. 6 GHz with a bandwidth of 3. 2 GHz above -10 dB loss.
参考文献
| [1] | Sun Z C,Geng Y H,Li J,Jing X B,Wang F S.Synth Met[J],1997,84:99 |
| [2] | Stejskal J,Hlavata D,Holler P,Trchova M,Prokes J,Sapurina I.Polym Int[J],2004,53(3):294 |
| [3] | XIA He-Sheng(夏和生),WANG Qi(王琪).Chem Res Appl(化学研究与应用)[J],2002,14(2):127 |
| [4] | Yang C,Chen C,Zeng Y.Spectrochim Acta Part A[J],2007,66(1):37 |
| [5] | WANG Zhong-Zhu(汪忠柱),SUN Tao(孙涛),LI Min-Quan(李民权).J Magn Mater Dev(磁性材料及器件)[J],2008,39(1):14 |
| [6] | REN Jie(任杰),WANG Zuo(王佐),TENG Xin-Rong(滕新荣).J Tongji Univ(Nat Sci)(同济大学学报(自然科学版))[J],2008,36(3):371 |
| [7] | Zhang L,Wan M.J Phys Chem B[J],2003,107(28):6 748 |
| [8] | WANG Zhe-Zhe(王哲哲),ZHAO Gao-Yang(赵高扬),LI Mei-Lian(李美莲),SHENG Shu-Yue(盛淑月),ZHANG Xiao-Lei(张晓磊).J Funct Mater(功能材料)[J],2008,6(39):892 |
| [9] | ZHOU Li(周莉),TIAN Yan-Wen(田彦文),ZANG Shu-Liang(臧数良).J Mol Sci(分子科学学报)[J],2008,24(3):170 |
| [10] | JIA Shuang-Lin(贾双琳),ZHANG Qiao-Lian(张巧莲),MENG Zhi-Yong(孟智勇).Chem Bioeng(化学与生物工程学报)[J],2008,25(2):69 |
| [11] | YANG You-Ping(杨幼平),HUANG Ke-Long(黄可龙),LIU Ren-Sheng(刘人生),WANG Li-Ping(王丽平),LIU Su-Qin(刘素琴),ZHANG Ping-Min(张平民).J Cent South Univ(Nat Sci)(中南大学学报(自然科学版))[J],2006,37(6):1 104 |
| [12] | YAN Hai-Yan(颜海艳),KOU Kai-Chang(寇开昌).Plast Sci Technol(塑料科技)[J],2008,36(7):70 |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%