用溶胶-凝胶法并经过不同温度(TA)处理而制备出La4/3Sr5/3Mn2O7多晶样品.零场下阻温关系测量表明,较低TA处理的样品有较高的绝缘体-金属转变温度Tp,而对较高TA处理的样品,其Tp在表面和体内有较大差别,表面上有较高的Tp值,且电阻率较低,但在体内Tp低且电阻率高.结合结构分析,我们认为,较高温度处理有利于Sr3Ti2O7相的形成,但太高温度(如高于1450℃)处理的样品,虽然以Sr3Ti2O7相为主,但其表面易形成(La,Sr)MnO3相.
参考文献
| [1] | S Jin et al.[J].Science,1994,264:413. |
| [2] | Morimoto Y;AsamitsuA;Kuwahara H;TokuraYandMatsuiY .[J].Nature,1996,380:141. |
| [3] | J Dho;WSKim;HS Choi;EOChi,NHHur .[J].Solid State Communications,2001,117:517. |
| [4] | R Mahesh;RMahendiran;A K Raychaudhuri;C N R Rao .[J].Journal of Solid State Chemistry,1996,122:448. |
| [5] | J Sloan;PDBattle;M A Green;MJRosseinskyandJFVente .[J].Journal of Solid State Chemistry,1996,138:135. |
| [6] | M T Calds;GGoglio;C Marhic;O Joubert M Lancin L Brohan.[J].International Journal of Inorganic Materials,2001(03):1169. |
| [7] | Morimoto Y;TomiokaY;Asamitsu A;H Kuwahara Tokura Y and Matsui Y .[J].Physical Review,1995,B51:3297. |
| [8] | 杨应平,李广,姜勇,曾祥勇,李建青,袁松柳.La2/3Ca1/3MnO3体系La位上Y掺杂及其对输运性质的影响[J].低温物理学报,2000(03):205-209. |
| [9] | 李志权,杨宏顺,任治安,余旻,柴一晟,李鹏程,曹烈兆.（La1-xSmx）0.185Sr0.15CuO4的输运性质的研究[J].低温物理学报,2001(01):39-43. |
| [10] | 尹道乐,齐志,许恒毅,王福仁,李传义.MgB2及高温超导体的强电子-声子耦合和输运性质[J].低温物理学报,2001(04):261-268. |
| [11] | 朱永文,方军,黄真,高秉钧.（La1-x Yx）0.5Sr0.5MnO3体系的结构和输运性质研究[J].低温物理学报,2003(02):151-156. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%