采用TFA-MOD方法在LaAlO3(001)单晶基片上制备了性能良好的YBCO超导薄膜:临界电流密度(Jc)可达3MA/cm2(77K,0T),超导转变温度Tc≈90K,转变宽度ΔTc=0.5K,其一次涂层厚度达338nm.通过X射线衍射(XRD)分析表明YBCO具有纯c-轴取向、无a-轴取向的晶粒存在.ω扫描分析表明该YBCO薄膜具有很好的面外外延性,其摇摆曲线的半高宽(FWHM)为0.653°. 用SEM分析也表明膜的表面无裂纹存在,表面平整,没有a轴晶粒生长.
参考文献
| [1] | Sun J W;Kim H S;Ji B K .[J].IEEE Transactions on Applied Superconductivity,2003,13:2539. |
| [2] | Iijima Y.;Kakimoto K.;Saitoh T. .Fabrication and transport characteristics of long length Y-123 coated conductors processed by IBAD and PLD[J].IEEE Transactions on Applied Superconductivity: A Publication of the IEEE Superconductivity Committee,2003(2):2466-2469. |
| [3] | King A.C.;Shoup S.S.;White M.K.;Krebs S.L.;Mattox D.M.;Polley T.;Darnell N.;Marken K.R.;Seung Hong;Czabaj B. .The progress made using the combustion chemical vapor deposition (CCVD) technique to fabricate YBa<SUB>2</SUB>Cu<SUB>3</SUB>O<SUB>7-x</SUB> coated conductors[J].IEEE Transactions on Applied Superconductivity: A Publication of the IEEE Superconductivity Committee,2003(2):2643-2645. |
| [4] | Yasuji Y;Suga T;Kurosaki H;Physica C .[J].,2000,341-348:2499-2500. |
| [5] | Guptal A;Jagannathan R;Cooper E I et al.[J].Applied Physics Letters,1988,52:2077. |
| [6] | Feenstra R;Lindemer T B;Budai J D .[J].Journal of Applied Physics,1991,69:6569. |
| [7] | Araki T.;Takahashi Y.;Yamigiwa K.;Yuasa T.;Iijima Y.;Takeda K.;Kim S.B.;Yamada Y.;Hirabayashi I. .Fabrication of YBa<SUB>2</SUB>Cu<SUB>3</SUB>O<SUB>7-x</SUB> filmson buffered metal tapes fired at low temperature by MOD method usingtrifluoroacetate salts[J].IEEE Transactions on Applied Superconductivity: A Publication of the IEEE Superconductivity Committee,2001(1):2869-2872. |
| [8] | Cui X M;Tao B W;Li Y R.[J].Rare Metal Materials and Engineering(in Chinese) |
| [9] | Takeshi A;Izumi H;Toshiharu N .[J].Superconductor Science and Technology,2004,17:135. |
| [10] | 孙国柱,吴培亨,吉争鸣,范世雄,杨森祖,许伟伟,康琳.在（100）SrTiO3上用PLD制备YBa2Cu3O7-δ/Eu2CuO4/LaNiO3三层结构[J].低温物理学报,2003(03):184-187. |
| [11] | 庄承钢,安玲,陈莉萍,丁莉莉,张开诚,陈晋平,徐军,冯庆荣,甘子钊.混合物理化学气相沉积法制备不锈钢衬底MgB2超导厚膜样品的韧度研究[J].低温物理学报,2005(02):103-110. |
| [12] | 贾璋,郭蕙璞,吕莹,王新峰,陈晋平,徐军,王晓楠,朱萌,冯庆荣.混合物理化学气相沉积法（HPCVD）制备的MgB2超导厚膜样品的成分分析[J].低温物理学报,2005(01):46-53. |
| [13] | 吉争鸣,李洪洋,孙国柱,许伟伟,吴培亨.高温超导薄膜微波表面电阻测量标准理论精度修正[J].低温物理学报,2005(03):211-214. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%