我们用射频磁控溅射方法,在Si(100)单晶衬底上生长MgO薄膜,借助X射线衍射(XRD)分析发现,我们获得了两种不同晶体结构的MgO薄膜,分别是常规的晶格常数为0.421nm的MgO薄膜和晶格常数为0.812nm的新结构的MgO薄膜.我们研究了溅射气压、衬底温度等工艺参数对两种晶体结构择取的影响.实验表明,高的溅射气压和高的衬底温度有利于晶格常数为0.812nm的新结构的MgO相的形成.在高的气压和温度下,我们制备出了晶格常数为0.812nm,具有很好的4次对称性的MgO外延薄膜.利用原子力显微镜(AFM)研究了这种薄膜的表面形貌.
参考文献
| [1] | X Y Chen;K H Wong;C L Mak .[J].Journal of Applied Physics,2002,91:1. |
| [2] | X.Y.Chen;K.H.Wong;C.L.Mak;J.M.Liu;X.B.Yin;M.Wang;LIU Z. G. .Orientation selective growth of MgO films on Si(100) by pulsed laser deposition[J].Applied physics, A. Materials science & processing,2002(5):703-706. |
| [3] | Jin-Hyo Boo;Soon-Bo Lee;Kyu-Sang Yu;Wonyong Koh;Yunsoo Kim .Growth of magnesium oxide thin films using single molecular precursors by metal-organic chemical vapor deposition[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,1999(12):63-67. |
| [4] | Myung M Sung;Chuleui Kim;Chang G Kim .[J].Journal of Crystal Growth,2000,210:651-654. |
| [5] | Jong-Gul Yoon;Kun Kim .[J].Applied Physics Letters,1995,66(20):15. |
| [6] | S. Chakrabarti;D. Ganguli;S. Chaudhuri .Preparation of hydroxide-free magnesium oxide films by an alkoxide-free sol-gel technique[J].Materials Letters,2003(29):4483-4492. |
| [7] | [Z].JCPDS-ICDD,1998,PDF#300794 |
| [8] | 杨名,崔旭高,杨森祖,张世远,康琳,吉争鸣,许伟伟,吴培亨.添加Ag的Nd0.7Sr0.3MnO3薄膜研究[J].低温物理学报,2002(04):248-253. |
| [9] | 曹春海,杨名,张世远,杨森祖,崔旭高,尤立星,吉争鸣,康琳,许伟伟.YBCO薄膜中自旋极化准粒子的注入效应[J].低温物理学报,2003(03):168-173. |
| [10] | 范世雄,许伟伟,刘庆国,吉争鸣,杨森祖,吴培亨.耐熔微掩膜法制备高温超导Josephson结[J].低温物理学报,2003(03):188-192. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%