采用传统的固相烧结工艺,制备了La0.75Ca0.25Mn1-xCrxO3(x=0,0.02,0.05,0.1)陶瓷样品,用X射线衍射对其微结构进行了分析,并测量了样品的铁磁性能.X射线谱显示样品为四方系晶体.ESR表明掺杂对样品朗德因子g几乎没有影响,而且样品总磁偶极矩的绝大部分是由自旋磁偶极矩贡献的.磁化曲线显示样品存在明显的自旋倾斜态,而掺杂可以削弱甚至破坏样品的自旋倾斜;样品热磁曲线表明,B位高掺杂导致样品晶格畸变从而使得样品磁化强度减小.
参考文献
| [1] | G.H.Jonker;J.H.Van Santen .[J].Physica,1956,16:707. |
| [2] | S.Jin;T.H.Tiefel;M.Mccormack;R.A.Fastnacht R.Raraesh and L.H.Chen .[J].Science,1994,264:413. |
| [3] | 陈解涛;田光善;林宗涵 .[J].低温物理学报,1998,20:245. |
| [4] | E.O.Wollen;W.C.Koehler .[J].Physical Review,1955,100:545. |
| [5] | 金克新,陈长乐,王永仓,赵省贵,袁孝,宋宙模.La2/3Ca1/3MnO3薄膜自旋输运特性研究[J].低温物理学报,2005(03):198-202. |
| [6] | A.Barnabe;A.Malgnan;M.Hervien;F.Damay C.Martin and B.Ravean .[J].Applied Physics Letters,1997,71:3907. |
| [7] | S. B. Ogale;Y. H. Li;M. Rajeswari .Columnar defect induced phase transformation in epitaxial La_(0.7)Ca_(0.3)MnO_(3) films[J].Journal of Applied Physics,2000(9):4210-4215. |
| [8] | V.S.Kolat;H.Gencer;S Atalay .[J].Physica B,2006,371:199. |
| [9] | 刘宁,严国清,郭焕银.La0.3Ca0.7Mn1-xWxO3（x=0.04,0.08,0.12）体系的电子自旋共振谱研究[J].低温物理学报,2007(02):81-85. |
| [10] | Ken-ichi Chahara;Toshiyuki Ohno;Masahiro Kasai;Yuzoo Kogono .[J].Applied Physics Letters,1993,63:1990. |
| [11] | H.LI Ju;C.Kwon;Qi Li;Q.L.Greene and T.Venkatesan .[J].Applied Physics Letters,1994,65:2108. |
| [12] | Bokov V A;Grigoryan N A;Bryzhina M F et al.[J].Physical Status Solidi,1968,28:835. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%