对马氏体球墨铸铁在不同pH值石英砂浆中的静载三体腐蚀磨损特性进行了试验研究，并与低铬白口铸铁进行了对比。结果表明：无论在静载三体磨料磨损或静载三体腐蚀磨损中，马氏体球墨铸铁均优于低铬白口铸铁。适当提高含硅量，有利于提高腐蚀磨损耐磨性，而且在酸性砂浆中效果较明显。
The three-body corrosion wear behaviors of martensitic ductile iron and low chromium white cast iron under the test conditions of different pH value slurries have been studied. The results show that the wear resistance of martensitic ductile iron excelled that of low chromium white cast iron no matter what test carried out in the static three-body abrasive wear or corrosion wear. It is in favour of increasing the corrosion-wear resistance when the silicon content is increased properly. Especially in the acidic slurry, the increasing effect is more obvious.
参考文献
| [1] | 吕振林;邓月声;饶启昌.基体组织状态对球墨铸铁磨料磨损性能的影响[J].铸造,1995(11):25-29. |
| [2] | 吕振林,邓月声,桑可正.马氏体球墨铸铁磨球及其应用[J].西安理工大学学报,1996(02):112-116. |
| [3] | 吕振林,周永欣,饶启昌.球墨铸铁磨料磨损与冲击疲劳特性[J].水利电力机械,1999(05):56-59,64. |
| [4] | Boys J W .Selection and use of wear tests for metals[J].Iron and Steel,1969,42(01):57-63. |
| [5] | 高义民;饶启昌;刘福玲.高铬铸铁三体腐蚀磨损过程中腐蚀与磨损的交互作用[J].铸造技术,1990(05):44-48. |
| [6] | 饶启昌;高义民;刘福玲 .高铬铸铁三体腐蚀磨损机理及影响因素的研究[J].西安交通大学学报,1992,26(01):81-90. |
| [7] | 高义民;饶启昌;刘福玲.铬系白口铸铁腐蚀磨损特性的研究[J].西安交通大学学报,1988(06):53-61. |
| [8] | Tomashov N D;Moore J J.The influence of grinding ball composition and wetgrinding conditions on metal wear Wear of Materials[A].New York:American Mechanical Engineering Society,1983:67-78. |
| [9] | Kim K Y;Bhattacharyya S.An electrochemical polarization tehcnique for evaluation of wear-corrosion in moving components under stress Wear of Materials[A].New York:American Mechanical Engineering Society,1981:772-778. |
| [10] | 宇佐美正;芹田阳 .高ク口厶白鑄鐵のサソ ド工口一ツヨ ンと耐蝕性との關系[J].鑄物,1978,50(05):281-286. |
| [11] | 任善之;汪孟春.铬系合金白口铸铁低应力浸蚀磨料磨损的研究[J].摩擦磨损,1983(03):23-31. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%