介绍了管线钢应力腐蚀破裂(SCC)的类型及特点,重点阐述了高pH SCC介质和近中性pH SCC介质的形成条件,并针对我国西气东输管道SCC研究提出了有关模拟环境试验条件的几点建议.
参考文献
| [1] | 左景伊.应力腐蚀破裂[M].西安:西安交通大学出版社,1985:1-3. |
| [2] | Kentish P J .Gas pipeline failures: Australian experience[J].British Corrosion Journal,1985,20(03):139-146. |
| [3] | 方丙炎,王俭秋,朱自勇,韩恩厚,柯伟.埋地管道在近中性pH和高pH环境中的应力腐蚀开裂[J].金属学报,2001(05):453-458. |
| [4] | Sridhar N;Lichtner P C;Dunn D S .Evolution of environment under disbonded coating on cathodically protected pipeline--preliminary modeling and experimental studies[R].CORROSION/98, NACE International, Houston, TX,1998. |
| [5] | Beavers J A;Jaske C E .Near-neutral pH SCC in pipelines: effects of pressure fluctuations on crack propagation[R].CORROSION/98, NACE International, Houston, TX,1998. |
| [6] | 李鹤林.天然气输送钢管研究与应用中的几个热点问题[A].北京:石油工业出版社,2001:3-18. |
| [7] | Sutcliffe J M;Fessler R R;Boyd W K et al.Stress corrosion cracking of carbon steel in carbonate solutions[J].Corrosion,1972,28(08):313-320. |
| [8] | Parkins R N;Greenwell B S.[J].Metal Science Journal,1977(11):405. |
| [9] | Davies D H;Burstein T .The effects of bicarbonate on the corrosion and passivation of iron[J].Corrosion,1980,36(08):416-422. |
| [10] | Fessler R R;Markworth A J;Parkins R N .Cathodic protection levels under disbonded coatings[J].Corrosion,1983,39(01):20-25. |
| [11] | Beavers J A;Berry W E;Parkins R N .Standard test procedure for stress corrosion cracking threshold stress determination[J].MP,1986,25(06):9-17. |
| [12] | Parkins R N;Markworth A J;HolbrookJ H .Hydrogen gas evolution from cathodically protected pipeline steel surfaces exposed to chloride-sulfate solutions[J].Corrosion,1988,44(08):572-580. |
| [13] | Parkins R N .Strain rate effects in stress corrosion cracking[J].Corrosion,1990,46(03):178-189. |
| [14] | Christman T K .Relationships between pitting, stress, and stress corrosion cracking of line pipe steels[J].Corrosion,1990,46(06):450-453. |
| [15] | Parkins R N;Singh P M .Stress corrosion crack coalescence[J].Corrosion,1990,46(06):485-499. |
| [16] | Harle B A;Beavers J A .Technical note: Low-pH stress corrosion crack propagation in API X-65 line pipe steel[J].Corrosion,1993,49(10):861-863. |
| [17] | Parkins R N;Belhimer E;Blanchard W K Jr .Stress corrosion cracking characteristics of a range of pipeline steels in carbonate-bicarbonate solution[J].Corrosion,1993,49(12):951-966. |
| [18] | Szklarska-Smialowska Z;Xia Z;Rebak R B .Technical note: Stress corrosion cracking of X-52 carbon steel in dilute aqueous solutions[J].Corrosion,1994,50(05):334-338. |
| [19] | Parkins R N;BlanchardJr WK;DelantyBS .Transgranular stress corrosion cracking of high-pressure pipelines in contact with solutions of near neutral pH[J].Corrosion,1994,50(05):394-408. |
| [20] | Mao X;Liu X;Revie R W .Pitting corrosion of pipeline steel in dilute bicarbonate solution with chloride Ions[J].Corrosion,1994,50(09):651-657. |
| [21] | A.K. Pilkey;S.B. Lambert;A. Plumtree .Stress Corrosion Cracking of X-60 Line Pipe Steel in a Carbonate-Bicarbonate Solution[J].Corrosion: The Journal of Science and Engineering,1995(2):91-96. |
| [22] | Charles E A;Parkins R N .Generation of stress corrosion cracking environments at pipeline surface[J].Corrosion,1995,51(07):518-527. |
| [23] | Rebak R B;Xia Z;Safruddin R et al.Effect of solution composition and electrochemical potential on stress corrosion cracking of X-52 pipeline steel[J].Corrosion,1996,52(05):396-405. |
| [24] | Urednicek M;Lambert S;Vosikovsky O .Stress corrosion cracking monitoring and control[R].Conf Pipeline Reliability, Calgary, Canada,1992. |
| [25] | J. Might;D.J. Duquette .Stress Corrosion Cracking of High-Purity Carbon Steel in Carbonate Solutions[J].Corrosion: The Journal of Science and Engineering,1996(6):428-434. |
| [26] | Ahrned T M;Lambert S B;Sutherby R et al.Cyclic crack growth rates of X-60 pipeline steel in a neutral dilute solution[J].Corrosion,1997,53(07):581-590. |
| [27] | L. J. Qiao;J. L. Luo;X. Mao .Hydrogen evolution and enrichment around stress corrosion crack tips of pipeline steels in dilute bicarbonate solution[J].Corrosion: The Journal of Science and Engineering,1998(2):115-120. |
| [28] | M. Yunovich;Z. Xia;Z. Szklarska-Smialowska .Factors influencing stress corrosion cracking of carbon steel in diluted bicarbonate environments[J].Corrosion: The Journal of Science and Engineering,1998(2):155-161. |
| [29] | B. Gu;J. Luo;X. Mao .Hydrogen-facilitated anodic dissolution-type stress corrosion cracking of pipeline steels in near-neutral pH solution[J].Corrosion: The Journal of Science and Engineering,1999(1):96-106. |
| [30] | X. -Y. Zhang;S. B. Lambert;R. Sutherby;A. Plumtree .Transgranular stress corrosion cracking of X-60 pipeline steel in simulated ground water[J].Corrosion: The Journal of Science and Engineering,1999(3):297-305. |
| [31] | B. Gu;W. Z. Yu;J. L. Luo;X. Mao .Transgranular stress corrosion cracking of X-80 and X-52 pipeline steels in dilute aqueous solution with near-neutral pH[J].Corrosion: The Journal of Science and Engineering,1999(3):312-318. |
| [32] | H. Asahi;T. Kushida;M. Kimura;H. Fukai;S. Okano .Role of microstructures on stress corrosion cracking of pipeline steels in carbonate-bicarbonate solution[J].Corrosion: The Journal of Science and Engineering,1999(7):644-652. |
| [33] | Wang X-Z;Revie R W;Parkins R N .Mechanistic aspects of stress corrosion crack initiation and early propagation[R].CORROSION/99, NACE International, Houston, TX,1999. |
| [34] | Brongers M.P.H.;Beavers J.A. .Effect of Hydrostatic Testing on Ductile Tearing of X-65 Line Pipe Steel with Stress Corrosion Cracks[J].Corrosion: The Journal of Science and Engineering,2000(10):1050-1058. |
| [35] | Danielson Mike J;Jones Russell H .Krist Kevin Effect of microstructure and microchemistry on the SCC behavior of pipeline steels in a high pH environment[R].CORROSION/2000, NACE International, Houston, TX,2000. |
| [36] | Lambert S B;Plumtree A;Sutherby R .Modeling of environmental crack growth in pipeline steel[R].CORROSION/2000, NACE International, Houston, TX,2000. |
| [37] | Jack T R;Erno B;Krist K .Generation of near neutral pH and high pH SCC environments on buried pipelines[R].CORROSION/2000, NACE International, Houston, TX,2000. |
| [38] | Danielson M J;Jones R H;Dusek Phil .Effect of microstructure and microchemistry on the SCC behavior of archival and modern pipeline steels in a high pH environment[R].CORROSION/2001, NACE International, Houston, TX,2001. |
| [39] | Wilmott M;Erno B;Jack T;Worthingharn R.The role of coating in the development of corrosion and stress corrosion cracking on gas transmission pipelines[A].New York:American Society of Mechanical Engineers,1998:399-408. |
| [40] | Sridhar Narasi;Dunn Darrel S;Anderko Andrzej.Prediction of conditions leading to stress corrosion cracking of gas transmission lines[M].Environmentally Assisted Cracking: Predictive Methods for Risk Assessment and Evaluation of Materials, Equipment, Structures:241-257. |
| [41] | Beavers J A;Durr C L;Delanty B S et al.Near-neutral pH SCC: crack propagation in susceptible soil environments[R].CORROSION/2001, NACE International, Houston, TX,2001. |
| [42] | Parkins R N .A review of stress corrosion cracking of high pressure gas pipelines[R].CORROSION/2000, NACE International, Houston, TX,2000. |
| [43] | Fessler R R;Krist K .Research challenges regarding stresscorrosion cracking of pipelines[R].CORROSION/2000, NACE International, Houston, TX,2000. |
| [44] | Johnson J T;Durr C L;Beavers J A .Effects of O2 and CO2 on near-neutral pH stress corrosion crack propagation[R].CORROSION/2000, NACE International, Houston, TX,2000. |
| [45] | 庄传晶;霍春勇.西气东输管线的风险预评价[A].北京:石油工业出版社,2001:498-507. |
| [46] | Parkins R N;Holroyd N J H;Fessler R R .Stress corrosion cracking of C-Mn steel in phosphate solutions[J].Corrosion,1978,34(08):253-262. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%