用分子沉积技术制备了PAH/PAA(TiO2)多层聚合物复合纳米粒子薄膜,为了增大薄膜自身的结合强度,采用加热的方式使其成膜动力发生转变.用紫外光谱及原子力显微镜(AFM)研究了薄膜的微观结构及其纳米摩擦学性能.结果表明,加热后薄膜中纳米粒子的长大导致薄膜表面粗糙度降低,同时提高了表面硬度,降低了薄膜表面摩擦力.
参考文献
| [1] | 任嗣利,杨生荣,张俊彦,张绪寿.自组装单分子膜的摩擦学研究进展[J].摩擦学学报,2000(05):395-400. |
| [2] | 张俊彦,杨生荣,薛群基.硅烷自组装膜及硅烷/二氧化钛复合膜的XPS表征与摩擦性能研究[J].摩擦学学报,2000(04):241-243. |
| [3] | Decher G;Hong J D;Schmitt J .Buildup of ultrathin multilayer films by a self-assembly process: I Consecutively alternating adsorption of anionic and cationic polyelectrolytes on charged surface[J].Thin Solid Films,1992,210-211:831-835. |
| [4] | Colvin V L;Schlamp M C;Alivisatos A P .Light-emitting diodes made from cadmium selenide nanocrystals and a semiconducting polymer[J].NATURE,1994,370(04):354-357. |
| [5] | 王德国,高芒来,张嗣伟.石英岩表面分子沉积膜的微观摩擦性能的试验研究[J].摩擦学学报,1999(01):28-32. |
| [6] | 王强斌,高芒来,张嗣伟.Au表面MD膜的纳米摩擦特性的实验研究[J].自然科学进展,1999(10):938. |
| [7] | WANG Qiang-bin;Gao Mang-lai;Zhang Si wei .Tribological application of molecular deposition (MD) films[J].Materials Science and Engineering C,1999(10):127-129. |
| [8] | WANG Qiangbin,GAO Manglai,ZHANG Siwei.Nanofriction properties of molecular deposition films[J].中国科学B辑（英文版）,2000(02):137-142. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%