用冲击试验和电化学充氢方法研究了长期服役的2.25Cr-1Mo钢的回火脆化和氢脆问题,并对试样进行了显微组织分析和断口电镜扫描.结果表明:回火脆化程度不高的母材对氢脆的影响较小,断口形貌为准解理和少量的沿晶断裂;回火脆化程度较严重的焊缝对氢脆的影响较大,断口形貌为沿晶断裂.对于母材,回火脆化与氢脆的关系为线性相加;对于焊缝,回火脆化大大加剧了氢脆的程度.
参考文献
| [1] | Erwin W E;Kerr J G .The use of quenched and tempered 2 1/4Cr-1Mo steel for thick wall reactor vessels in petroleum refinery processes:an interpretive review of 25 years of research and application[J].WRC Bulletin,1982,275:1-63. |
| [2] | T/G Ⅱ of the subcommittee on hydrogen embrittlement of JPVRC .Embrittlement of pressure vessel steels in high temperature, high pressure hydrogen environment[J].WRC Bulletin,1985,305:9-21. |
| [3] | 柳曾典;林建鸿 .在役加氢反应器挂片试板材质劣化状况的评定[R].上海:华东理工大学,1998. |
| [4] | 林建鸿;柳曾典;吴东棣 .热壁加氢反应器运行过程中的材质劣化问题[J].石油化工设备技术,1997,18(05):4-9. |
| [5] | 山田;铃木;高野 .Cr-Mo钢的回火脆性与氢脆性的关系[J].压力技术,1981,19(03):64. |
| [6] | 韩光伟;罗涤;杨凤兰 等.氢与回火脆化对2.25Cr-1Mo钢局部脆断应力的影响[J].钢铁研究学报,1996,8(05):36-41. |
| [7] | McMahon Jr C J .Hydrogen-induced intergranular fracture of steel[J].Engineering Fracture Mechanics,2001,68(06):773-788. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%