研究了PTFE填充量对高岭土基矿物聚合物复合材料的力学性能和摩擦磨损性能的影响,利用XRD、SEM分析了材料的微观结构和磨损表面形貌.结果表明:填充PTFE对矿物聚合物材料的力学性能会有一定程度的降低,但可以有效改善复合材料的摩擦磨损性能,当PTFE体积分数为30%时,摩擦因数和磨损率均达到最低,分别为0.429和1.22×10-5mm3/N·m;当PTFE含量较高时,磨损机理除了磨粒磨损外还有对偶件的粘着转移.
参考文献
| [1] | Davidovits J .Geopolymers: ingorgnic polymeric new materials[J].Journal of Thermal Analysis,1991,37:1633-1656. |
| [2] | Davidovits J .Geoplymer: ingorgnic polymeric new materials[J].Journal of Mater Educ,1994,16:91-139. |
| [3] | Davidovits J;Davidovics M;Davidovics N .Process for obtaining a geopolymeric alumino-silicate and products thus obtained[P].US:5342595,1994-8-30. |
| [4] | Davidovits J;Davidovics M .Geopolymer room temperature ceramic matrix for composites[J].Ceramic Engineering and Science Proceedings,1988,9:835-842. |
| [5] | 袁鸿昌;江尧忠 .地聚合物材料的发展及其在我国的应用前景[J].硅酸盐通报,1998,2:46-51. |
| [6] | H. Xu;J. S. J. V. Deventer .The geopolymerisation of alumino-silicate minerals[J].International Journal of Mineral Processing,2000(3):247-266. |
| [7] | Hua Xu;Jannie S.J. Van Deventer .Microstructural characterisation of geopolymers synthesised from kaolinite/stilbite mixtures using XRD, MAS-NMR, SEM/EDX, TEM/EDX, and HREM[J].Cement and Concrete Research,2002(11):1705-1716. |
| [8] | 高红霞,商全义,张贵州,高学敏.（Ni-P）-SiC-PTFE化学复合镀层摩擦性能研究[J].表面技术,2003(02):31-32,35. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%