利用非均匀形核法制备了铜包覆纳米SiC复合粉体,通过XRD、SEM、EDS、TEM等手段对复合粉体进行了微观测试和表征.结果表明:纳米SiC颗粒表面的铜包覆层均匀、连续,铜晶粒平均粒径约38 nm,部分氧化成Cu2O,氧化率为11.54%.用质量分数为0.5%的PEG-20000作为分散剂,能有效地分散纳米SiC颗粒,并阻止包覆在纳米SiC颗粒表面的铜晶粒过度长大.
参考文献
| [1] | 曹茂盛;关长斌;徐甲强.纳米材料导论[M].哈尔滨:哈尔滨工业大学出版社,2001:128. |
| [2] | A. M. Davidson;D. Regener .A comparison of aluminium-based metal-matrix composites reinforced with coated and uncoated particulate silicon carbide[J].Composites science and technology,2000(6):865-869. |
| [3] | Shu KM.;Tu GC. .The microstructure and the thermal expansion characteristics of Cu/SiCp composites[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2003(1/2):236-247. |
| [4] | 师瑞霞,尹衍升,周春华,马来鹏,李嘉.钴包覆纳米Al2O3/TiCp复相陶瓷的力学性能及其增韧机制[J].机械工程材料,2004(11):28-31. |
| [5] | 王耐艳 .Cu-纳米TiB<,2>原位复合材料的制备及摩擦磨损性能[D].浙江大学,2002. |
| [6] | Ju-Xian Zhang;Long-Qiao Gao .Nanocomposite powders from coating with heterogeneous nucleation processing[J].Ceramics International,2001(2):143-147. |
| [7] | 范启义,凌国平,郦剑.化学镀铜法制备纳米Cu-Al2O3复合粉体的研究[J].材料科学与工艺,2002(04):357-361. |
| [8] | Rui Zhang;Lian Gao;Jingkun Guo .Preparation and characterization of coated nanoscale Cu/SiC_p composite particles[J].Ceramics International,2004(3):401-404. |
| [9] | 黄惠忠.纳米材料分析[M].北京:化学工业出版社,2003:244. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%