累积损伤方法已被广泛应用于复合材料的各种结构损伤分析及强度预测中.对累积损伤方法在纤维增强复合材料机械连接接头性能研究中的应用进行了分析论述,主要包含应力分析中的有限元建模、失效判定准则及损伤过程中材料性能退化三大部分.并对该分析方法在今后研究的动向进行了展望.
参考文献
| [1] | Tsujimoto Y;Wilson D .Elasto-plastic failure analysis of composite bolted joints[J].Journal of Composite Materials,1986,20:236-252. |
| [2] | Lie S T;Yu G;Zhao Z .Analysis of mechanically fastenedcomposite joints by boundary element methods[J].COMPOSITES,2000,31:693705. |
| [3] | Chang F K;Scott R A .Failure strength of nonlinearly elastic composite laminates containing a pin loaded hole[J].Journal of Composite Materials,1984,18:464-477. |
| [4] | Chang F K;Chang K Y .A progressive damage model for laminated composites containing stress concentrations[J].Journal of Composite Materials,1987,21:834-855. |
| [5] | Chang F K;Chang K Y .Post-failure analysis of bolted composite joints in tension or shear-out mode failure[J].Journal of Composite Materials,1987,21:809-833. |
| [6] | Bulent Murat Icten;Ramazan Karakuzu .Progressive failure analysis of pin-loaded carbon-epoxy woven composite plates[J].Composites science and technology,2002(9):1259-1271. |
| [7] | 华玉,郦正能,寇长河.复合材料单钉接头的损伤累积模拟[J].航空学报,1995(02):153. |
| [8] | Camanho P P;Matthews F L .A progressive damage model for mechanically fastened joints in composite laminates[J].Journal of Composite Materials,1999,23:2248-2249. |
| [9] | Tserpes K I;Labeas G;Papanikos P et al.Stength prediction of bolted joints in graphite/epoxy composite laminates[J].Composites Part B:Engineering,2002,33:521-529. |
| [10] | Kermanidis T;Labeas G;Tserpes K I.Finite element modeling of damage accumulation in bolted composite joints under incremental tensile loading[A].Barcelona,2000 |
| [11] | Shokrieh M M;Lessard L B .Progressive fatigue damage modeling of composite materials,part Ⅰ:modeling[J].Journal of Composite Materials,2000,34:1056-1080. |
| [12] | Shokrieh M M;Lessard L B .Progressive fatigue damage modeling of composite materials,part Ⅱ:material characterization and model verification[J].Journal of Composite Materials,2000,34:1081-1116. |
| [13] | Perugini P;Riccio A;Scaramuzzino F.Three-dimensional progressive damage analysis of composite joints[A].Stirling Scotland:Civil-Comp Press,2001 |
| [14] | Riccio A;Scaramuzzino F.Influence of damage onset and propagation on the tensile structural behavior of protruding composite joints[A].Patras,2002 |
| [15] | Kim SJ.;Kim JH.;Hwang JS. .Progressive failure analysis of pin-loaded laminated composites using penalty finite element method[J].AIAA journal,1998(1):75-80. |
| [16] | Yamada S E;Sun C T .Analysis of laminate strength and its distribution[J].Journal of Composite Materials,1978,12:275-284. |
| [17] | Hashin Z .Failure criteria for unidirectional fiber composites[J].Journal of Applied Mechanics,Transactions ASME,1980,47:329-335. |
| [18] | Hashin Z .Fatigue failure criteria for combined cyclic stress[J].International Journal of Fracture,1981,17:101-109. |
| [19] | P. PAPANIKOS;K. I. TSERPES;SP. PANTELAKIS .Modelling of fatigue damage progression and life of CFRP laminates[J].Fatigue & Fracture of Engineering Materials and Structures,2003(1):37-47. |
| [20] | Shokrieh M M;Lessard L B;Poon C.Three-dimensional progressive failure analysis of pin/bolt loaded composite laminates[A].Florence,1996 |
| [21] | Wen-Hwa Chen;Shyh-Shiaw Lee;Jyi-Tyan Yeh .Three-dimensional contact stress analysis of a composite laminate with bolted joint[J].Composite Structures,1995(3):287-297. |
| [22] | Hung CL.;Chang FK. .BEARING FAILURE OF BOLTED COMPOSITE JOINTS .2. MODEL AND VERIFICATION[J].Journal of Composite Materials,1996(12):1359-1400. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%