应用取向分布函数研究和分析了退火对异步轧制高纯铝箔微取向的影响.结果表明:在异步轧制的试样中产生较强的{001},《110》旋转立方织构和{102}《uVW》织构.异步轧制后退火的高纯铝箔试样中,立方{001}《100》织构组分的形成存在一个"阈值温度",此温度与异步轧制的速比成反比,随着速比的增加,"阈值温度"降低,这与异步轧制提高高纯铝箔的形变储能有关.适宜的速比,相应的形变量和与之相匹配的退火工艺,可以获得强的立方织构.
参考文献
| [1] | Montheillet F;Cohen M;Jonas J J .Axial stresses and texture development during the torsion testing of Al,Cu and α-Fe[J].Acta Materialia,1984,32:2077-2089. |
| [2] | Hjelen J;Qrsund R;Nes E .On the origin of recrystallization textures in aluminum[J].Acta Metallurgica Et Materialia,1991,39:1377-1380. |
| [3] | 吕爱强,黄涛,王福,左良.异步轧制高纯铝箔冷轧织构沿板厚的分布规律[J].中国有色金属学报,2003(01):56-59. |
| [4] | 吕爱强,蒋奇武,王福,左良,梁志德.异步轧制对高纯铝箔冷轧织构的影响[J].金属学报,2002(09):974-978. |
| [5] | 梁志德;徐家桢;王福.织构材料三维取向分析术--ODF分析[M].沈阳:东北工学院出版社,1986 |
| [6] | Montheillet F;Gilormini P;Jonas J J .Relation between axialstresses and texture development during torsion testing:a simplified theory[J].Acta Materialia,1985,33:705-717. |
| [7] | 毛卫民;赵新兵.金属的再结晶与晶粒长大[M].北京:冶金工业出版社,1994 |
| [8] | 毛卫民.金属材料的晶体学织构与各向异性[M].北京:科学出版社,2002 |
| [9] | 哈宽富.金属力学性质的微观理论[M].北京:科学出版社,1983 |
| [10] | Hirsch J;Nes E;Lücke K .Rolling and recrystallization texture in directionally solidified aluminum[J].Acta Materialia,1987,35:427-438. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%