使用高能行星式球磨机,在不同水溶液中球磨了金属锰粉末,通过XRD和TEM对生成相种类及其形貌进行研究.结果表明:球磨一段时间后,在机械力作用下,锰与水反应并获得了粒径为30～100nm的γ-Mn3O4;继续球磨,γ-Mn3O4进一步氧化或发生晶型转变;而且加入微量HCl和MnSO4极大地加快了反应速度,而加入微量NaOH则抑制了反应速度,并用Mn-H2O的电位-pH图对这些现象进行了解释.
参考文献
| [1] | Vesselin M;Titus F;Wayne B D et al.Highly crystalline Mn2O3 or Mn3O4 manganese oxides[P].US 0022959,2001-09-20. |
| [2] | Liu Yangping;Yuan Junjun;Lin Peiyan et al.Catalytic activity of nanocrystalline manganese oxidefor CO oxide[J].物理化学学报,1999,12(01):82-86. |
| [3] | Zhang Weixin;Wang Cheng;Zhang Xiaomin et al.Low temperature synthesis of nanocrystalline Mn3O4 by a solovthermalmethod[J].Solid State Ionics,1999,117:331-335. |
| [4] | A. Dierstein;H. Natter;F. Meyer .ELECTROCHEMICAL DEPOSITION UNDER OXIDIZING CONDITIONS (EDOC): A NEW SYNTHESIS FOR NANOCRYSTALLINE METAL OXIDES[J].Scripta materialia,2001(8-9):2209-2212. |
| [5] | Raphael Janot;Daniel Guerard .One-step synthesis of maghemite nanometric powders by ball-milling[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2002(1/2):302-307. |
| [6] | 李运姣,李洪桂,赵中伟,孙培梅,霍广生,孙召明.机械活化-湿化学合成LiMn2O4的组成、结构与表征[J].中国有色金属学报,2004(z1):112-117. |
| [7] | 曹金华;张志胜;张超 等.磨机中物料分布的分界面研究[J].电子工业专用设备,1999,28(04):12-15. |
| [8] | 陶新永,张孝彬,孔凡志,林森,程继鹏,黄宛真,李昱,刘芙,许国良.PEG辅助氧化锌纳米棒的水热法制备[J].化学学报,2004(17):1658-1662. |
| [9] | 薛娟琴,王成刚,刘小勇.以硫酸锰为原料制备四氧化三锰的理论分析[J].西安建筑科技大学学报（自然科学版）,2000(03):297-299. |
| [10] | 陈鼎,陈振华,陈刚,黄培云.固液反应球磨制备TiAl,NiAl和FeAl金属间化合物[J].湖南大学学报(自然科学版),2003(02):20-24,98. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%