以Ti(C,N)基金属陶瓷粉末为研究对象,采用三组不同配比的蜡基粘结剂,考查了注射成形溶剂脱脂工艺中脱脂温度、脱脂时间、试样厚度及溶剂种类和浓度等参数对坯块脱脂率的影响,对溶剂脱脂过程中脱脂坯尺寸的变化及可溶性组元的最大脱除率等也作了初步的研究.结果表明:采用3#粘结剂的脱脂坯溶剂脱脂缺陷最少,较适合于溶剂脱脂;采用正庚烷对该粘结剂的脱脂坯进行50℃溶剂脱脂,经过6 h可脱除70%以上的石蜡,连通孔道基本形成.
参考文献
| [1] | German R M.Powder injection molding[M].Princeton,NJ:MPIF,1990 |
| [2] | Bankovic D R;German R M.Optimization of debinding cycles in powder injection molding[A].Princeton:MPIF,1990 |
| [3] | Yang Wei-Wen;Yang Kai-Yuan .Solvent debinding mechanism for alumina injection molded compacts with water-soluble binders[J].Ceramics International,2003,29:745-756. |
| [4] | Li Songlin,Huang Baiyun,Qu Xuanhui,Li Yimin.Solvent de-binding of water-soluble binder in powder injection moulding[J].中国有色金属学会会刊（英文版）,1999(03):578-581. |
| [5] | 刘宁.钇对金属陶瓷力学性能和组织的影响[J].中国稀土学报,1997(01):80. |
| [6] | Qi F.;Kang S. .A study on microstructural changes in Ti(CN)-NbC-Ni cermets[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1998(1/2):276-285. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%