采用热压烧结法制备了氧化铝/透辉石复相陶瓷材料,分析了复合材料的微观结构,测试了复合材料的断裂韧度、硬度和抗弯强度与透辉石颗粒含量的对应关系.结果表明:在28 MPa、1 450℃×30 min条件下热压烧结制备的复相陶瓷材料,其抗弯强度、断裂韧度均有明显提高,最高达到442.5 MPa和4.76 MPa·m1/2.
参考文献
| [1] | 林营,杨海波,王芬.直接金属氧化法制备SiCp/Al2O3-Al复合材料[J].机械工程材料,2005(06):27-29,47. |
| [2] | C. C. Anya .Microstructural nature of strengthening and toughening in Al2O3-SiC(p) nanocomposites[J].Journal of Materials Science,1999(22):5557-5567. |
| [3] | 邓建新;艾兴 .SiC晶须增韧Al2O3陶瓷组成及其断裂行为的研究[J].材料科学与工程学报,1995,13(01):33-36. |
| [4] | Tekeli S .High temperature ductility and cavitation behaviour of hot isostatically pressed (HIP)ZrO2/Al2O3 composite containing 40 wt% Al2O3[J].Ceramics International,2003,29(02):169-174. |
| [5] | Jayaseelan D.;Awaji H.;Gnanam FD.;Nishikawa T. .Pressureless sintering of sol-gel derived alumina-zirconia composites[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1998(1/2):265-270. |
| [6] | 赵永红,李光新,马新沛.MgO-Al2O3-SiO2系高强度微晶玻璃的晶化行为与力学性能[J].硅酸盐学报,2003(04):413-416. |
| [7] | 卡恩 R W;哈森 P;克雷默 E J.材料科学与技术丛书(第11卷)--陶瓷的结构与性能[M].北京:科学出版社,1998 |
| [8] | M. Sathiyakumar;F. D. Gnanam .Role of wollastonite additive on density, microstructure and mechanical properties of alumina[J].Ceramics International,2003(8):869-873. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%