对TC11钛合金燕尾榫连接结构在低周和高低周复合载荷作用下的断口特征进行了分析.结果表明:在微动环境下,微动磨损面上有表面金属掉块和不均匀的磨损擦伤,磨损表面出现腐蚀坑以及损伤区呈现层状及山丘状的塑性变形;在高低周复合载荷情况下,疲劳源处疲劳辉纹呈现以河流花样为主的复杂疲劳条纹,在裂纹扩展阶段,河流花样比较杂乱,裂纹扩展方向相对无序,每个低周周期中的疲劳台阶也不明显.
参考文献
| [1] | Ruiz C;Boddington PHB;Chen C .An investigation of fatigue and fretting in a dovetail joint[J].Experimental Mechanics,1984,24(03):208-217. |
| [2] | Szolwinsk M P;Farris T N .Mechanics of fretting fatigue crack formation[J].Wear,1996,198(01):93-107. |
| [3] | Rooke D P;Jones D A .Stress intensity factors in fretting fatigue[J].Journal of Strain Analysis,1979,14(01):1-6. |
| [4] | 周仲荣.Vincent L微动磨损[M].北京:科学出版社,2002 |
| [5] | 刘道新,何家文.微动疲劳影响因素及钛合金微动疲劳行为[J].航空学报,2001(05):454-457. |
| [6] | Fu YQ.;Batchelor AW.;Liu DX.;Zhu XD.;He JW.;Xu KW.;Loh NL. .Improvement in fretting wear and fatigue resistance of Ti-6Al-4V by application of several surface treatments and coatings[J].Surface & Coatings Technology,1998(2/3):193-197. |
| [7] | 王世洪,梁佑明,沈桂琴.TC11钛合金微动磨损及疲劳防护工艺的探讨[J].航空学报,1996(03):379. |
| [8] | 卫中山,王珉,李亮,刘六法,丁文江.TC4合金微动疲劳损伤研究[J].机械工程材料,2006(01):30-32. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%