采用单根硼纤维拔出模型分析了硼纤维拔出过程界面剪切应力的分布;同时设计了一种单纤维拔出试样制备方法,并测试了不同硼纤维/环氧复合材料界面抗剪强度.结果表明:界面脱粘前,在纤维包埋起始端部和包埋末端界面存在剪切应力极大值,纤维包埋中间部位剪切应力较小;采用液体丁腈橡胶改性环氧树脂的硼纤维/环氧复合材料界面抗剪强度比未改性环氧树脂的提高了135%.
参考文献
| [1] | Piggott M R .Why interface testing by single-fibre methods can be misleading[J].Composites Science and Techonology,1997,57:965-974. |
| [2] | Koichi Goda .The role of interfacial debonding in increasing the strength and reliability of unidirectional fibrous composites[J].Composites science and technology,1999(12):1871-1879. |
| [3] | Zeng Q D;Ling L;Wang Z L .Statistical strength of unidirectional composites and the effect of the interfacial shear strength[J].Composites Science and Techonology,1996,56:1191-1200. |
| [4] | 陈祥宝.聚合物基复合材料手册[M].北京:化学工业出版社,2004 |
| [5] | Jones R;Molent L .Application of constitutive modelling and advanced repair technology to F111C aircraft[J].Computers & Structures,2004,66:145-157. |
| [6] | 孙曼灵.环氧树脂应用原理与技术[M].北京:机械工业出版社,2002 |
| [7] | Chua P S;Piggott M R .The glass fiber-polymer interface:Ⅰ-Theoretical consideration for single fiber pull-out tests[J].Composites Science and Techonology,1985,22:33-42. |
| [8] | 杨庆生.复合材料细观结构力学与设计[M].北京:中国铁道出版社,2000 |
| [9] | Marotzke C .Influence of the fiber length on the stress transfer from glass and carbon fibers into a thermoplastic matrix in the pull-out test[J].Composites Interfaces,1993,1:153-166. |
| [10] | Tripathi D;Jones R F .Measurement of the load-bearing capability of the fiber/matrix interface by single-fiber fragmentation[J].Composites Science and Techonology,1997,57:925-935. |
| [11] | 王零森;罗雄;陈熙 等.复合材料的界面强度及测定方法[J].材料研究学报,1994,8(04):372-377. |
| [12] | 陈平,张岩.热固性树脂的增韧方法及其增韧机理[J].复合材料学报,1999(03):19-22. |
| [13] | 吴培熙;张留城.聚合物共混改性[M].北京:中国轻工业出版社,1998 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%