以钼、硅、碳粉末为原料,采用湿法混合和原位反应热压一次复合工艺制备了MoSi2以及含不同体积分数原位SiC颗粒的SiCP/MoSi2复合材料,并研究了原位SiC颗粒对该材料室温断裂韧度的影响.结果表明:复合后的SiCP/MoSi2室温断裂韧度大幅度提高,原位SiC颗粒可以细化MoSi2基体晶粒,减少和消除脆性的SiO2玻璃相,并阻碍SiCP/MoSi2复合材料断裂时的裂纹扩展而造成裂纹的偏转和桥接.
参考文献
| [1] | Sastry M L;Suryanarayanan R;Jerina K L .Consolidation and mechanical properties of MoSi2 baseed materials[J].Materials Science and Engineering,1995,92:881-890. |
| [2] | Lu T C;Evan A G .Matrix cracking in intermetallic composites caused by thermal expansion mismatch[J].Acta Metallurgica Et Materialia,1991,39(08):1883-1890. |
| [3] | Petrovic J J .ZrO2 reinforced MoSi2 matrix composites[J].Ceramic Engineering and Science Proceedings,1991,12(9-10):1633-1636. |
| [4] | 孙岚,潘金生,清华大学,北京.TiC颗粒增韧MoSi2基复合材料的力学性能[J].材料工程,2001(09):31-34. |
| [5] | 李爱兰,曾燮榕,李贺军,李龙,熊信柏.Nb增韧MoSi2基复合材料的研究进展[J].材料工程,2002(02):6-9,26. |
| [6] | Costa e Silva A;Kaufman M J .Applications of in situ reaction to MoSi2 based materials[J].Materials Science and Engineering A,1995,195:75-77. |
| [7] | 寇开昌,杨延清,艾云龙,陈彦,康沫狂.MoSi2-WSi2复合体系的自蔓延燃烧合成[J].稀有金属材料与工程,2000(03):190-192. |
| [8] | 张来启,孙祖庆,张跃,杨王玥,陈光南.原位SiC颗粒增强MoSi2基复合材料的显微组织和力学性能[J].金属学报,2001(03):325-331. |
| [9] | 郜剑英,江莞,李建林,吴历斌.二硅化钼合金化及掺杂改性的研究进展[J].中国钼业,2003(04):22-27. |
| [10] | Aikin R M .Strengthening of discontinuously reinforced MoSi2 composites at high temperatures[J].Materials Science and Engineering A,1992,155:121-133. |
| [11] | 刘伯威,潘进,樊毅,张金生.SiC颗粒强韧化MoSi2复合材料[J].复合材料学报,2002(01):59-63. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%