主要对异步轧制AZ31镁合金板材的显微组织和晶粒取向进行了研究,以探讨提高镁合金板材塑性变形能力的途径.结果表明:由于异步轧制时板材的变形量比常规轧制时的大,其动态再结晶进行得比较完全,因此异步轧制有利于AZ31镁合金板材晶粒的细化与均匀化;并且改变异步轧制的工艺条件,能够在一定程度上改善镁合金板材中的(0002)基面织构取向,使织构得到软化,从而提高镁合金的塑性变形能力.
参考文献
| [1] | Aghion E.;Bronfin B. .Magnesium Alloys Development towards the 21~(st) Century[J].Materials Science Forum,2000(0):19-28. |
| [2] | K. Iwanaga;H. Tashiro;H. Okamoto;K. Shimizu .Improvement of formability from room temperature to warm temperature in AZ-31 magnesium alloy[J].Journal of Materials Processing Technology,2004(0):1313-1316. |
| [3] | Y. Chino;J.-S. Lee;K. Sassa .Press formability of a rolled AZ31 Mg alloy sheet with controlled texture[J].Materials Letters,2006(2):173-176. |
| [4] | Kalidindi SR. .Modeling anisotropic strain hardening and deformation textures in low stacking fault energy fcc metals[J].International Journal of Plasticity,2001(6):837-860. |
| [5] | Poss R .Sheet metal production of magnesium[J].Materials Science Forum,2003,419-422:327-336. |
| [6] | Perez-Prado M T;valle J A;Contreras J M et al.Microstructural evolution during large strain hot rolling of an AM60 Mg alloy[J].Scripta Materialia,2004,50:661-665. |
| [7] | Valle J A;Prado M T;Ruano O A .Texture evolution during large-strain hot rolling of the AZ61 Mg alloy[J].Materials Science and Engineering,2003,A355:68-78. |
| [8] | Su-Hyeon Kim;Bong-Sim You;Chang Dong Yim .Texture and microstructure changes in asymmetrically hot rolled AZ31 magnesium alloy sheets[J].Materials Letters,2005(29/30):3876-3880. |
| [9] | Watanabe H;Mukai T;Ishikawa K .Differential speed rolling of an AZ31 magnesium alloy and the resulting mechanical properties[J].Journal of Materials Science,2004,39:1477-1480. |
| [10] | 李尧.异步轧制对3004铝合金变形织构及制耳率的影响[J].中国有色金属学报,1997(02):113-117. |
| [11] | 陈振华;夏伟军;严红革.变形镁合金[M].北京:化学工业出版社,2005 |
| [12] | 钟家湘;郑秀华;刘颖.金属学教程[M].北京:北京理工大学出版社,1995:304-305. |
| [13] | 于九明,于大克,穆晓森,潘大炜,朱泉.大延伸异步连轧实验研究[J].钢铁,1999(02):29-30. |
| [14] | 陈振华,夏伟军,程永奇,傅定发.镁合金织构与各向异性[J].中国有色金属学报,2005(01):1-11. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%