采用搅拌摩擦焊方法对6 mm厚的2219铝合金板进行焊接,研究了2219铝合金的搅拌摩擦焊工艺和主要焊接参数对焊缝成形和接头力学性能的影响.结果表明:在旋转速度1250～1400 r·min-1,焊接速度100～140 mm·min-1时,可获得性能良好的焊接接头;对2219铝合金搅拌摩擦焊接后再固溶时效处理可有效消除接头软化区,提高接头强度.
参考文献
| [1] | Kallee S W;Thomas W M;Nicholas E D.Friction stir weld-ing of light weight materials[A].,2000:123-129. |
| [2] | 栾国红,关桥.搅拌摩擦焊--革命性的宇航制造新技术[J].航天制造技术,2003(04):16-23. |
| [3] | Horng-Yu Wu;Shyong Lee;Jian-Yih Wang .Solid-state bonding of iron-based alloys, steel-brass, and aluminum alloys[J].Journal of Materials Processing Technology,1998(1/3):173-179. |
| [4] | John A. Wert .Microstructures of friction stir weld joints between an aluminium-base metal matrix composite and a monolithic aluminium alloy[J].Scripta materialia,2003(6):607-612. |
| [5] | H. J. Liu;H. Fuju;M. Maeda;K. Nogi .Tensile properties and fracture locations of friction-stir-welded joints of 2017-T351 aluminum alloy[J].Journal of Materials Processing Technology,2003(3):692-696. |
| [6] | 姜澜,魏绪钧,姚广春,王德全.铝合金搅拌摩擦焊研究现状及应用[J].材料导报,2003(06):70-72. |
| [7] | 杨宗辉,孙孝纯,王笑川,何建军.搅拌摩擦焊与铝船制造革命[J].电焊机,2004(02):9-13. |
| [8] | 张平,王卫欣,赵军军.7A52铝合金搅拌摩擦焊接头特征分析[J].兵器材料科学与工程,2004(06):38-42. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%