通过气相输运平衡技术,严格控制生长条件和气氛,制备了化学组分均匀、光学质量优异的近化学计量组分Er:LiNbO3晶体.通过对吸收边、喇曼谱及红外OH-吸收谱的测量,发现吸收边"蓝移";OH-吸收带显著减弱;Er:LiNbO3晶体中的E模(152cm-1)和A1模(632cm-1)的线宽也明显变窄.这些特征都证实了得到的Er:LiNbO3晶体已接近于化学计量组分,经过计算,其Li+含量达到49.7mol%.
参考文献
| [1] | Jer Mann F;Simon M;Krzig E .Photorefractive Properties of Congruent and Stoichiometric Lithium Niobate at High Light Intensities[J].Journal of the Optical Society of America,1995,B12:2066. |
| [2] | 姚江宏,陈亚辉,许京军,张光寅,朱圣星.近化学计量比铌酸锂晶体周期极化畴反转特性研究[J].物理学报,2002(01):192-196. |
| [3] | Abdi F.;Bourson P.;Fontana MD.;Polgar K.;Aillerie M. .Electro-optic properties in pure LiNbO3 crystals from the congruent to the stoichiometric composition[J].Journal of Applied Physics,1998(4):2251-2254. |
| [4] | Wohlecke M;Corradi G;Betzler K .Optical Methods to Characterize the Composition and Homogeneity of Lithium Niobate Single Crystals[J].Journal of Applied Physiology,1996,B63:323. |
| [5] | Malovichko G I;Grachev V G;Kokanyan E P et al.Characterization of Stoichiometric LiNbO3 Grown from Melts Containing K2O[J].Journal of Applied Physiology,1993,A56:103. |
| [6] | Kong Yongfa;Chen Xiaojun;Xu Jingjun;Zhang Guangyin;Zhang Wanlin .OH~- absorption spectra of pure lithium niobate crystals[J].Journal of Physics. Condensed Matter,1999(9):2139-2143. |
| [7] | Schirmer O F;Theiemann O;Wohlecke M .Defects in LiNbO3-I Experimental Aspects[J].Journal of Physics and Chemistry of Solids,1991,52(01):185. |
| [8] | Iyi N;Kitamura K;Izumi F et al.Comparative Study of Defect Structures in Lithium Niobate with Defferent Compositions[J].Journal of Solid State Chemistry,1992,101:340. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%