采用RF-PECVD方法,在P-a-SiC:H薄膜沉积技术基础上,通过逐步减小碳、硼的掺杂浓度,增大氢稀释率,使材料从非晶态向微晶态转变,在获得本征微晶材料之后,再逐步增大硼掺杂浓度,得到P型微晶硅薄膜材料(暗电导率为5.22×10-3S/cm,光学带隙大于2.0eV).在这个过程中可以明显观察到碳、硼抑制材料晶化的作用.
参考文献
| [1] | Yu ZR.;Carreno MNP.;Pereyra I. .Wide optical band gap window layers for solar cells[J].Solar Energy Materials and Solar Cells: An International Journal Devoted to Photovoltaic, Photothermal, and Photochemical Solar Energy Conversion,2001(1/4):155-162. |
| [2] | Rath JK.;Schropp REI. .Incorporation of p-type microcrystalline silicon films in amorphous silicon based solar cells in a superstrate structure[J].Solar Energy Materials and Solar Cells: An International Journal Devoted to Photovoltaic, Photothermal, and Photochemical Solar Energy Conversion,1998(1/2):189-203. |
| [3] | Droz C;Vallat-SauvainE;Bailat J.Application of Raman Spectroscopy for the Microstructure Characterization in Microcrystalline Silicon Solar Cells[A].,2001:2917-2920. |
| [4] | Kondo M.;Nasuno Y.;Mase H.;Wada T.;Matsuda A. .Low-temperature fabrication of microcrystalline silicon and its application to solar cells[J].Journal of Non-Crystalline Solids: A Journal Devoted to Oxide, Halide, Chalcogenide and Metallic Glasses, Amorphous Semiconductors, Non-Crystalline Films, Glass-Ceramics and Glassy Composites,2002(Pt.1):108-112. |
| [5] | 陈治明.非晶半导体材料与器件[M].北京:科学出版社,1991:123. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%