用提拉法成功生长出了优质的Cr3+:Gd3Sc2Ga3O12晶体,测定了室温下的吸收光谱和不同温度下的荧光光谱,计算了晶场参数,发现荧光峰值及晶场参数与以前文献报道的均不相同.吸收光谱中,在458.5nm和642.5nm出现了较强的宽带吸收峰,分别对应于Cr3+的4A2→4T1和4A2→4T2的吸收跃迁,在678nm处又叠加了一个非常弱的吸收峰,对应于4A2→2T1的吸收跃迁.测试了晶体从7K到室温的荧光光谱和荧光寿命,在650～850nm范围内出现了宽带荧光,对应于Cr3+的4T2→4A2的发射跃迁.随着温度的升高,荧光峰向长波方向移动,荧光峰半高宽增大,室温下其荧光峰值在732nm,半高宽约为80nm.低温(7K)下的荧光谱中,在694nm处观察到了尖而锐的R线(零声子线),对应于Cr3+的2E→4A2的发射跃迁.由于温度猝灭效应,随着温度升高,晶体的荧光寿命降低,室温下荧光寿命约为114μs.计算了晶场强度参数Dq/B=2.49,4T2零声子能级与2E能级的间距△E为204cm-1,这些参数表明Cr3+处在较弱的晶场中,有利于4T2→4A2的宽带跃迁,Cr:GSGG晶体是较为理想的可调谐激光工作物质.
参考文献
| [1] | Struve B;Huber G;Laptev V V et al.Tunable Room-temperature CW Laser Action in Cr3+:GdScGa-Garnet[J].Applied Physics B-Lasers and Optics,1983,30:117-120. |
| [2] | Struve B;Huber G et al.Laser Action and Broad Band Fluorescence in Cr3+:GaScGa-Garnet[J].Applied Physics B-Lasers and Optics,1982,28:235-236. |
| [3] | 李运奎.新型激光晶体Gd3（In,Ga）2Ga3O12：Cr3+的发光[J].中国激光,1990(04):236. |
| [4] | Li YK.;Qin QH.;Ge YX.;Chang Y.;Wang XG.;Yin ST. .Czochralski growth and optical spectral properties of GInGG : Cr3+ single crystal[J].Progress in Crystal Growth and Characterization of Materials,2000(1/4):201-209. |
| [5] | Li YK.;Yuan YQ.;Yin ST.;Du KM.;Gabel K. .Luminescence and color centers from CNGG : Cr3(+) crystal grown by Czochralski method[J].Journal of Crystal Growth,2000(4):867-873. |
| [6] | 刘琳.GGG（Ga,Mg,Zr）：Cr可调谐激光晶体的研制[J].人工晶体学报,1989(04):279. |
| [7] | Bass M.;Weichman L.S.;Vigil S.;Brickeen B.K. .The temperature dependence of Nd<sup>3+</sup> doped solid-state lasers[J].IEEE Journal of Quantum Electronics: A Publication of the IEEE Quantum Electronics and Applications Society,2003(6):741-748. |
| [8] | Struve B;HuberG .TheEffect of the Crystal Field Strength on the Optical Spectra of Cr3+ in Gallium Garnet Laser Crystals[J].Applied Physics B-Lasers and Optics,1985,36:195-201. |
| [9] | 袁剑辉,程玉民,张振华.Ca3Al2Ge3O12：Cr3+的光谱性质及晶场参数计算[J].物理化学学报,2005(09):1059-1062. |
| [10] | W.R.Romanowski;S.Golab .Optical study of chromium doped LaGaO3 single crystal[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,1999(1/2):22-26. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%