以Al(NO3)3和Y(NO3)3为原料,采用共沉淀法制备出粒度大小为60～100nm,颗粒呈球形的纯相YAG纳米粉.研究了前驱物在不同条件下热处理对YAG纳米粉体性能的影响,并对前驱物在焙烧过程中的物相变化进行了观察,发现延长前驱物在低温下的干燥时间会导致晶粒尺寸增大,而采用在晶化温度前后分别进行保温的方法可在较低的温度获得纯相的YAG粉体.对比了焙烧温度和保温时间对产物粒度的影响,结果表明:在保证粉体晶化完全的前提下,升高焙烧温度比延长保温时间对晶粒尺寸有更显著的影响.
参考文献
| [1] | Corman G S .Creep of Yttrium Aluminum Garnet Single Crystal[J].Journal of Materials Science Letters,1993,12:1033. |
| [2] | DE WITH G;VAN DIJK H J A .Translucent Y3Al5O12 Ceramics[J].Materials Research Bulletin,1984,19(12):1669. |
| [3] | Daikuzono N .Present and Future of Medical YAG Laser[J].Review of Lasers Engineering,1993,21(08):894. |
| [4] | Ji-Guang Li;Takayasu Ikegami .Co-precipitation synthesis and sintering of yttrium aluminum garnet (YAG) powders: the effect of precipitant[J].Journal of the European Ceramic Society,2000(14/15):2395-2405. |
| [5] | Li Xia;Liu Hong;Wang Jiyang .Preparation of YAG:Nd Nano-suzed Powder by Co-precipitation Method[J].Materials Science and Engineering A,2004,379:347. |
| [6] | 王介强,陶珍东,孙旭东.无机溶胶凝胶法制取Y2O3纳米微粒[J].中国稀土学报,2003(01):15-18. |
| [7] | 方小龙,杨传芳,陈家镛.湿化学工艺条件对ZrO2（Y2O3）超细颗粒团聚的影响[J].硅酸盐学报,1998(06):732-739. |
| [8] | 张芳,秦小梅,修稚萌,由健,孙旭东.钇铝硝酸盐共熔制备YAG微粉[J].功能材料,2002(01):88-89. |
| [9] | 许凤秀,李霞.YAG纳米粉体的制备技术研究进展[J].中国陶瓷工业,2004(03):38-41. |
| [10] | 黄朝红,王爱华,殷绍唐,蔡伟,秦晓.Nd：YAG透明陶瓷制备技术的研究进展[J].硅酸盐学报,2003(09):873-877. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%