本文采用高温固相反应法在800℃合成了NaBa4Al2B8O18Cl3多晶粉末,探索了生长NaBa4Al2B8O18Cl3晶体的助熔剂,采用顶部籽晶技术分别以NaF和LiCl作助熔剂成功生长出NaBa4Al2B8O18Cl3透明晶体,晶体最大尺寸为22mm×22mm×15mm.粉末倍频测试测得NaBa4Al2B8O18Cl3晶体的粉末倍频强度为KDP的0.5～1.0倍.
参考文献
| [1] | Chen C;Wu B;Jiang A et al.A New-type Ultraviolet SHG Crystal-β-BaB2O4[J].Scientia Sinica,1985,B28:235-243. |
| [2] | Chen C;Wu B;Jiang A et al.New Nonlinear-optical Crystal:LiB3O5[J].Journal of the Optical Society of America,1989,B6:616-621. |
| [3] | Wu Y;Sasaki T;Nakai S et al.CsB3O5:A New Nonlinear Optical Crystal[J].Applied Physics Letters,1993,62:2614-2615. |
| [4] | Takatomo Sasaki;Yusuke Mori;Ikuo Kuroda;Satoshi Nakajima;Kotoko Yamaguchi;Seiya Watanabe;Sadao Nakai .Caesium Lithium Borate: a New Nonlinear Optical Crystal[J].Acta Crystallographica. Sect.C, Section C. Crystal Structure Communications,1995(11):2222-2224. |
| [5] | Chen C T;Wang Y B;Wu B C et al.Design and Synthesis of an Ultraviolet-transparent Nonlinear Optical Crystal Sr2Be2B2O7[J].NATURE,1995,373:322. |
| [6] | Mei L;Wang Y;Chen C et al.Nonlinear Optical Materials Based on MBe2BO3F2(M =Na,K)[J].Journal of Applied Physics,1993,74:7014-7015. |
| [7] | Hu Z;Higashiyama T;Yoshimura M et al.Flux Growth of the New Nonlinear Nptical Crystal:K2Al2B2 O7[J].Journal of Crystal Growth,2000,212:368-371. |
| [8] | Hu Z;Yoshimura M;Muramatsu K et al.A New Nonlinear OpticalCrystal-BaAlBO3F2(BABF)[J].Japanese Journal of Applied Physics,2002,41:L1131-L1133. |
| [9] | 李云阁 .非线性光学晶体Na3La9O3(BO3)8和BaAlBO3F2(BABF)的生长与性能研究[D].中国科学院研究生院,2005. |
| [10] | Kurtz S K;Perrry T T .A Powder Technique for the Evaluation of Nonlinear Optical Materials[J].Journal of Applied Physicy,1968,39:3798-3813. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%