通过对SS400钢板的一系列分析，得出了造成SS400钢板冷弯试验后出现裂纹的原因，即主要是钢板表面附近具有一定大小的硅酸盐夹杂物所致。
The SS400 plate was studied with the series of tests. The results indicate that the cause of the crack onthe surface plate during bend test results from the biger si-salt inclusion near surface of plate.