通过金相、X射线衍射及扫描电镜(SEM/EDX),结合电化学测试手段,研究了Cu-Cr合金在3.5%NaCl+NH3溶液中的腐蚀行为,并探讨了NH3浓度对其腐蚀性能的影响.结果表明:Cu-Cr合金中铜相较铬相易腐蚀,其腐蚀速率随NH3浓度的增加而增大.
参考文献
| [1] | Prasad V V S;Rao U R K;Misra R D K .Electroslag Crucible Melting of Age Hardening Copper-Chromium Alloy[J].Materials Science and Technology,1995,11:1306-1309. |
| [2] | Niu Y;Gesmundo F;Douglass D L .The Air Oxidation of Two-Phase Cu-Cr Alloys at 700 ℃-900 ℃[J].Oxidation of Metals,1997,48:357-359. |
| [3] | FU Guang-yan,NIU Yan,WU Wei-tao,GUAN Heng-rong.Oxidation of two-phase Cu-Cr alloys with different microstructures[J].中国有色金属学会会刊(英文版),2001(03):333-336. |
| [4] | ZHANG Cheng-yu,WANG Jiang,ZHANG Hui,YANG Zhi-mao,DING Bing-jun.Deoxidization of CuCr25 alloys prepared by vacuum induction melting[J].中国有色金属学会会刊(英文版),2001(03):337-339. |
| [5] | 李金平,罗守靖,纪松,胡伟晔,龚朝晖.爆炸烧结CuCr触头材料的性能[基金项目] 宁波市科委青年基金资助项目（9711004）[J].中国有色金属学报,2001(z1):98-101. |
| [6] | 朱小龙,林乐耘,徐杰,雷廷权.形变对70Cu-30Ni合金腐蚀行为的影响[J].中国有色金属学报,1997(02):79-81,85. |
| [7] | 朱小龙;雷廷权 .70Cu-30Ni合金海水腐蚀产物膜形成过程[J].金属学报,1997,33(12):1257-1260. |
| [8] | 曹丽云;由向群;王丽梅 .塑性变形及晶粒度对装饰铜合金腐蚀性能的影响[J].辽宁工学院学报,1994,14(02):10-13. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%