采用ODF方法，对3种在不同热轧终轧温度下得到的Ti+Nb处理的高强IF钢板退火织构进行了研究。结果表明：奥氏体区终轧时，随着终轧温度降低，γ纤维织构及其｛111｝〈112〉组分有所增强，热轧卷取组织的晶粒细化和二相粒子的弥散析出是织构变化的原因。
The annealing textures of interstitial free and high strengthsteel sheets treated by Ti & Nb at three finishing temperatures have been examined by means of ODF respectively. Results show that when the steel is hot rolled at austenite region the intensities of γ-fibre axis texture and its ｛111｝〈112〉 constituents increase with the drop of finishing temperatures because the grains of the hot rolling and coiling microstructure are refined and the second phase particles precipitated.
参考文献
| [1] | Takachi .Development in High Strength Hot and Cold rolled Steels for Automotive Application[Z].Hot and Cold Rolled Sheet Steels,1988. |
| [2] | 赵子苏;毛卫民;余永宁 等.轿车用高强IF钢的开发和应用[J].钢铁研究学报,1998,1(zk):91. |
| [3] | 关小军;王先进 .超低碳高强度烘烤硬化钢板退火组织及性能[J].北京科技大学学报,1993,15(06):580. |
| [4] | Wang Li;Yuan Mingsheng;Zhao Zisu .The Effect of Ti Amounts on the Mechanical Properties of the High Strength Ti+Nb-IF Cold Rolled Batch Annealed Steels[Z].Advanced Automobile Materials,1997. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%