Factors Affecting Adhesive Strength of Multi-Arc Ion Plated TiN Coating

选择 W6Mo5Cr4V2、3Cr2W8V和GCr15等材料研究了多弧离子镀TiN涂层与基体的结合力。结果表明，基体表面粗糙度越小、硬度越高，涂层与基体的结合力越好，涂层厚度以2．5～3．5μm为最佳，含V量高的基体和具有强烈TiN(111)择优取向的涂层结合力好。

The adhesive strengths of the multi-arc ion plated TiN coatings with substrates W6Mo5Cr4V2,3Cr2W8V and GCr15 were studied. The results showed that the lower the roughness of the substrate surface, the higher the adhesive strength was. And with the increase of vanadium content and the hardness of the substrate, the adhesion was getting improved. The strong TiN (111)preferred orientation had favourable effect on adhesion.

参考文献

[1]	黄子勋.电镀理论[M].北京:中国农业机械出版社,1982
[2]	王福贞.表面沉积技术[M].北京:机械工业出版社,1989
[3]	Rickerby DS;Bull SJ .Engineering with surface coatings:The role of coating microstructrue[J].Surface and Coatings Technology,1989,39-40:315-328.
[4]	陈国平.薄膜物理与技术[M].南京:东南大学出版社,1993
[5]	宋人娟.多弧离子镀TiN低温涂层的研究[J].金属热处理,1994(06):17.

上一张下一张

计量

下载量()
访问量()

作者相关

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网