用均匀腐蚀法和电化学法研究了碳钢(A3)在pH值5.0的硝酸铀酰溶液中的腐蚀行为.均匀腐蚀试验结果表明,碳钢在pH值5.0硝酸铀酰溶液中发生非电化学腐蚀,使溶液酸度降低,导致铀酰离子水解,在碳钢表面形成了水合氧化铀沉积膜.动电位阳极极化试验结果显示,碳钢的腐蚀电位随扫描电位速率的增加向阴极方向移动,UO2+2的沉积对碳钢的阴极反应有抑制作用.均匀腐蚀后的样品,经XRD、XPS分析证实,沉积膜主要为铀酰离子的氧化物沉淀.
参考文献
| [1] | Ogura K;Sato K .Cathodic dissolution of the passive film on iron-Ⅰ.Kinetics and mechanism[J].Electrochimica Acta,1979,25:857-862. |
| [2] | Lorbeer P;Lorenz W J .The kinetics of iron dissolution and passi vation in solutions containing oxygen[J].Electrochimica Acta,1979,25:375-381. |
| [3] | Videm K;Koren A M .Corrosion,passivity,and pitting of carbons teel in aqueous solutions of HCO3-,CO2,and Cl[J].Corrosion Science,1993,49(09):746-754. |
| [4] | 倪铁军,王文西,蔡兰坤.水溶液中硅酸盐缓蚀剂与碳钢表面氧化物相互作用的研究[J].腐蚀与防护,2001(11):479-482. |
| [5] | J. Engelhardt;G. Marx .Contact corrosion measurements on the pair UO_(2+x) and carbon steel 1.0330 in brines and bentonite porewater with respect to direct waste disposal[J].Journal of Nuclear Materials: Materials Aspects of Fission and Fusion,1999(1/2):161-168. |
| [6] | 唐任寰;刘元方;张青莲.锕系-锕系后元素[M].北京:科学出版社,1998:173. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%