对碱性锌酸盐体系电镀Zn-Fe合金阴极电流效率的影响因素进行了系统的研究,并分析了镀层中铁原子的引入对Zn-Fe合金电镀阴极电流效率的影响原因及合金镀层中铁含量与阴极电流效率的关系,以期通过控制镀液组成及工艺条件在一定程度上提高阴极电流效率.增加电镀液中锌铁离子总摩尔浓度,提高镀液中锌铁离子摩尔比,降低铁离子浓度,适当控制阴极电流密度,升高镀液温度均可提高锌铁合金电沉积的阴极电流效率.添加剂ZFA的加入使Zn-Fe合金电镀的阴极电流效率降低.合金镀层中引入Fe明显降低了电沉积的阴极电流效率,镀层中的Fe含量从0升高至0.73%,合金电沉积的阴极电流效率却从79.48%降低至68.23%.这是由于碱性溶液中,氢气在金属Fe上析出的过电势明显小于在金属Zn上的过电势,使析氢容易进行引起的.
参考文献
| [1] | Fratesi R;Roventi G;Giuliani G et al.Zinc-cobalt alloy electrodeposition from chloride baths[J].Journal of Applied Electrochemistry,1997,27:1088-1094. |
| [2] | Y. Liao;D. R. Gabe;G. D. Wilcox .A study of zinc-iron alloy electrodeposition using a rotating cylinder hull cell[J].Plating & Surface Finishing,1998(3):60-66. |
| [3] | Paatsch W;Kautek W;Sahre M .Corrosion behavior and mechanical properties of plated Zn-alloys[J].Transactions of the Institute of Metal Finishing,1997,75(06):216-218. |
| [4] | Short N R;Dennis J K .Corrosion resistance of zinc-alloy coated steel in construction industry environments[J].Transactions of the Institute of Metal Finishing,1997,75(02):47-52. |
| [5] | Bikulcius G .Control of thickness of corrosion - resistant Zn- Fe,Zn-Co and Zn-Ni coatings[J].Plating and Surface Finishing,1997,84(08):31-32. |
| [6] | 王云燕,彭文杰.锌酸盐镀锌阴极电流效率的研究[J].电镀与环保,2003(06):12-16. |
| [7] | 张允诚;胡如南;向荣.电镀手册(上册)[M].北京:国防工业出版社,1997:95-154. |
| [8] | 屠振密.电镀合金原理与工艺[M].北京:国防工业出版社,1993:231-243. |
| [9] | 查全性.电极过程动力学导论(第2版)[M].北京:科学出版社,1987:407-415. |
| [10] | 巴德A·J;福克纳L R;谷林瑛;吕鸣祥,宋诗哲.电化学方法原理及应用[M].北京:化学工业出版社,1986:615. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%