起泡是有机涂层失效的主要形式之一.综述了国内外对有机涂层起泡微观机制的研究情况,分析了有机涂层起泡发生的过程,并从渗透压起泡、阳极起泡、阴极起泡、应力起泡、电渗透起泡等微观机制角度阐述了有机涂层的失效行为.
参考文献
| [1] | Gonzalez S.;Caceres F.;Fox V.;Souto RM. .Resistance of metallic substrates protected by an organic coating containing aluminum powder [Review][J].Progress in Organic Coatings: An International Review Journal,2003(4):317-323. |
| [2] | 刘斌 .有机涂层/基底金属体系腐蚀电化学行为研究[D].中国科学院金属研究所,2003. |
| [3] | 张忠礼.钢结构热喷涂防腐蚀技术[M].北京:化学工业出版社,2004 |
| [4] | 李言涛 .喷涂锌铝覆盖层在海洋环境中的腐蚀行为及失效机理[D].中国科学院海洋研究所,1999. |
| [5] | Funke W .Toward a unified view of the mechanism responsible for paint defects by metallic corrosion[J].Industrial and Engineering Chemistry:Product Research and Development,1985,24(03):343-347. |
| [6] | ZHANG Xian-cheng,XU Bin-shi,WANG Hai-dou,WU Yi-xiong.Failure behavior of protective organic coatings under corrosive conditions[J].中国有色金属学会会刊（英文版）,2004(z1):395-404. |
| [7] | 张显程,巩建鸣,涂善东,孔凡玉.涂层缺陷对涂层失效与基体腐蚀行为的影响研究[J].材料科学与工程学报,2003(06):922-926. |
| [8] | Van Der Weijde D H;Van Westing E P M;De Wrr J H W .EIS measurements on artificial blisters in organic coatings[J].Electrochimica Acta,1996,41(07):1103-1107. |
| [9] | 刘斌,李瑛,林海潮,曹楚南.防腐蚀涂层失效行为研究进展[J].腐蚀科学与防护技术,2001(05):305-307. |
| [10] | Payer J H;Michal G M .Processes of blister formation in electrodeposited coatings on steel[J].Society of Automotive Engineers Transactions,1991,100(05):1123-1134. |
| [11] | Storfer Stanley J Yuhas .Mechanism of blister formation in organic coatings[J].Materials Performance,1989,28(07):35-41. |
| [12] | Hansen;Charles M .New developments in corrosion and blister formation in coatings[J].Progress in Organic Coatings,1995,26(02):113-120. |
| [13] | Pommersheim J M;Nguyen T.Prediction of blistering in coating systems[A].Washington,DC:American Chemical Society,1998:137-150. |
| [14] | T. Nguyen;J.B. Hubbard;J.M. Pommersheim .Unified Model for the Degradation of Organic Coatings on Steel in a Neutral Electrolyte[J].JCT,1996(855):45-56. |
| [15] | Leidheiser H .Corrosion of Painted Metals--A Review[J].Corrosion,1982,38(07):374-383. |
| [16] | Appleman B R .Painting over soluble salts:A perspective[J].Journal of Protective Coatings Linkings,1987,10(04):68-82. |
| [17] | Touyeras;George F;Cabala B .Study of adherence loss for paint films coated onto polymeric substrates by induced blistering[J].Journal of Adhesion Science and Technology,1997,11(02):263-279. |
| [18] | Funke W .Toward a unified view of the mechanism responsible for paint defects by metallic corrosion[J].Ind Eng Chem Prod Res,1985,24(03):343-347. |
| [19] | Funke W .Blistering of paint films and filiform corrosion[J].Progress in Organic Coatings,1981,9(01):29-46. |
| [20] | Van Der Meel-Lerk L A;Heertjes P M .Blistering of varnish films on substrates induced by salts[J].Journal of Oil and Colour Chemists Association,1975,58:79-84. |
| [21] | Van Der Meer-Lerk L A;Heertjes P M .Influence of pressure on blister growth[J].Journal of Oil and Colour Chemists Association,1981,64:30-38. |
| [22] | Van Der Meer-Lerk L A;Heertjes P M .Mathematical model of growth of blisters in varnish films on different substrates[J].Journal of Oil and Colour Chemists Association,1979,62(06):256-263. |
| [23] | Nguyen T;Martin J W.Modes and mechanism of degradation of expoxy-coated reinforcing steel in a marine environment[M].London,1996:491-502. |
| [24] | Mc Cafferty E .Use of activity coefficients to calculate the equilibrium conditions within a localized corrosion cell on iron[J].Journal Electrochemical Society,1981,128(01):39-44. |
| [25] | Jones D A.Principles and Prevention of Corrosion[M].USA:Macmillan Publishing Company,1992:568. |
| [26] | Leidheiser H.Corrosion Control by Organic Coatings[M].Houston Tex:National Association of Corrosion Engineers,1981:103-110. |
| [27] | Non-osmotically-induced blistering phenomena on metal[J].Journal of Protective Coatings & Linings,1998(3):17-34. |
| [28] | Nguyen T;Hubbard J B;Mc Fadden G B A .Mathematically model for the cathodic blistering of organic coatings on steel immersed in electrolytes[J].Journal of Coating Technology,1991,794(63):43-52. |
| [29] | Rodriguez Leidheiser V S Jr H .Cathodic blistering of two alkyd paints[J].Coatings Technology,1988,60(757):45-51. |
| [30] | R.F.Hamade;D.A.Dillard .Assessing the effects of shear,compression,and peel on the cathodic degradation of elastomer-to-metal adhesive bonds[J].International Journal of Adhesion & Adhesives,2005(2):147-163. |
| [31] | Chuang T J;Nguyen T;Lee S .Micro-mechanic model for cathodic blister growth in painted steel[J].Coatings Technology,1999,71(895):75-85. |
| [32] | Martin J W;Embree E;Tsao W .Non-osmotic defect controlled cathodic disbondment of a coating from a steel substrate[J].Journal of Coating Technology,1990,62(790):25-33. |
| [33] | Brunt N A .Blistering of paint layers as an effect of swelling by water[J].Journal of the Oil and Colour Chemists Association,1964,47(01):31-42. |
| [34] | Chuang T J;Nguyen T;Li S.Anon-osmotic blister growth model in coating systems[A].Vienna Austria,1997:203-209. |
| [35] | 孙廷耀.涂层起泡探析[J].涂料工业,1999(03):41-44. |
| [36] | Greenfield D;Scantlebury D.The Protective Action of Organic Coatings on Steel:A Review[J].The Journal of Corrosion Science and Engineering,2000(03):5. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%