采用直流和直流脉冲电源对AZ91D镁合金进行微弧氧化处理,得到具有相同厚度的氧化膜,通过显微硬度测定、扫描电镜观察和极化曲线测试等手段研究了不同电源对微弧氧化膜层性能的影响.结果表明:直流电源下膜层的生长速率大于脉冲直流电源下的;用不同电源处理得到的氧化膜,硬度基本相同;脉冲直流电源下氧化膜的表面形貌、耐蚀性好于直流电源下的,高频下氧化膜的表面形貌、耐蚀性优于低频下的氧化膜.
参考文献
| [1] | 刘正;张奎;曾小勤.镁基轻质合金理论基础及其应用[M].北京:机械工业出版社,2002 |
| [2] | Wu C T;Lu F H .Corrosion resistance of BaTiO3 films prepared by plasma electrolutic oxidation[J].Surface and Coatings Technology,2002,166:31. |
| [3] | Gnedenkov S V;Khrisanfova 0 A;Zavidnaya A G et al.Production of hard and heat-resistant coatings 0n aluminum using a plasma micro-discharge[J].Surface and Coatings Technology,2000,23:24. |
| [4] | Timoshenko AV;Magurova YV .Investigation of plasma electrolytic oxidation processes of magnesium alloy MA2-1 under pulse polarisation modes[J].Surface & Coatings Technology,2005(2/3):135-140. |
| [5] | Yerokhin AL;Shatrov A;Samsonov V;Shashkov P;Pilkington A;Leyland A;Matthews A .Oxide ceramic coatings on aluminium alloys produced by a pulsed bipolar plasma electrolytic oxidation process[J].Surface & Coatings Technology,2005(2/3):150-157. |
| [6] | Yerokhin A L;Nie X;Leyland A et al.Plasma electrolysis of surface engineering[J].Surface and Coatings Technology,1999,122:81-82. |
| [7] | 蒋百灵,张先锋,朱静.铝合金镁合金微弧氧化陶瓷层的形成机理及性能[J].西安理工大学学报,2003(04):297-302. |
| [8] | Van T B;Brown S D;Wirtz G P .Mechanism of anode spark deposition[J].American Ceramic Society of Bulletin,1977,56(06):563-566. |
| [9] | Krysmann W;Kurze P;Dittrich H G .Process charaeteristics and parameters of oxidation by spark discharge(ANOF)[J].Crystal Research and Technology,1984,19(07):973-979. |
| [10] | Kurze P;Krysmann W;Schreekenbach J et al.Colored ANOF layers on aluminum[J].Crystal Research and Technology,1987,22(01):53-58. |
| [11] | 郭洪飞,安茂忠,徐莘,霍慧彬.电流密度对镁合金微弧氧化过程及氧化陶瓷膜性能的影响[J].稀有金属材料与工程,2005(10):1554-1557. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%