为了解拉丝用低温磷化膜的成膜机理,研究了其电位-时间(φ-t)曲线变化规律,并采用扫描电镜(SEM)观察了磷化膜的形貌,用X射线能谱对磷化成分进行了分析.结果表明,φ-t曲线和磷化膜生长过程可分为三个阶段:磷化第一阶段约15 s,电位快速正移,出现零星分布、长约10μm的磷化膜小晶粒;磷化第二阶段约45 s,电位快速负移,出现直径大小约10μm的薄片层状晶粒团,单个晶粒直径约5μm,晶粒与基底间存在底膜;磷化第三阶段约840 s,电位缓慢正移直至稳定,前期有大量晶粒形成并不断长大,后期晶粒显著长大,但数量变化不大,磷化膜不断增厚直至磷化反应终止.
参考文献
| [1] | Sinha P K;Feser R .Phosphate coating on steel surfaces by itn electrochemical method[J].Surface and Coatings Technology,2002,161:158-168. |
| [2] | Lazzarotto L;Marechal C;Dubar L et al.The effects of processing bath parameters on the quality performance of zinc phosphate stearate coatings[J].Surface Engineering and Coating Technology,1999,122(03):94-100. |
| [3] | Burokas V.;Bikulcius G.;Martusiene A. .The influence of hexametaphosphate on formation of zinc phosphate coatings for deep drawing of steel tubes[J].Surface & Coatings Technology,1998(3):233-236. |
| [4] | 刘福生;王晟 .金属拔丝用中温磷化液的研制[J].化工时刊,1999,12(08):17-20. |
| [5] | 向鸿照,陈伟,陈天朗,肖慎修.Zn-Mn-Ca-Ni系中温磷化液的研究[J].材料保护,2004(05):13-15,41. |
| [6] | 江静华,张旭海,蒋建清,马爱斌,方峰.冷成型模具低温锌系磷化[J].材料保护,2002(05):32-33. |
| [7] | 隋永强,梁成浩.低温锌系磷化液的研究[J].表面技术,2004(05):37-39. |
| [8] | 方峰,于金,顾菡妍,曹文奎,蒋建清.金属拉丝用低温快速磷化处理工艺研究[J].东南大学学报（自然科学版）,2005(02):253-256. |
| [9] | 方峰,顾菡妍,曹文奎,涂益友,蒋建清.金属拉丝用低温快速磷化液的研制与应用[J].材料保护,2005(02):53-56. |
| [10] | 暨调和;黄季煌 .常(低温)加速磷化过程φ-t曲线的研究[J].电镀与环保,1994,14(04):11-15. |
| [11] | 徐惠芳.低温磷化膜形成过程的研究[J].材料保护,1995(06):17. |
| [12] | JOHN DONOFRIO .ZINC PHOSPHATING[J].Metal finishing,2000(6):64-80. |
| [13] | Ang K F .Development of phosphate coatings on mild steel[J].TIMF,1991,69(02):58-65. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%