利用STEM和EDAX对Sialon晶粒的生长形貌及固溶体Z值进行分析发现,不同发育形态的六方晶型Sialon晶粒及晶粒内不同位置均具有不同的Al3+固溶含量,该研究结果表明,根据原料配比中或烧结体中的Al3+含量来计算Sialon材料的固溶Z值是不确切的.