本文研制了一种K2O-B2O3-Al2O3-SiO2系统AgX光色玻璃。此玻璃具有较宽的热处理制度，在610～670℃和2～8h之间进行热处理，热处理温度和时间对玻璃的光色性质影响不大。所以，可作为大面积无色差的平板光色玻璃材料来进一步研究。
The heterophasic photochromic glass containing silver halide in K2O-B2O3-Al2O3-SiO2 system was studied in this paper，and the photochromic glass has wide ranges in thermal treatment temperature and thermal treatment time.The results indicate that the photochromic properties of the glasses are almost similar when the glass was heat treated at 610～670℃for 2～8hours. So they can avoid the chromic aberration in the glass as a result of the thermal treatment process difference.Hence，they can be used to study the flat photochromic galss in the large area.