研究了重结晶碳化硅高温材料的凝胶注模成型.着重讨论了SiC粉体的分散性、悬浮体的流变性、沉降行为以及烧结机理.结果表明,选用适量的分散剂TMAH调整浆料pH＝11.9附近可制备出固相体积分数高达70%的SiC浓悬浮体.沉降实验表明,该浓悬浮体中粗细SiC颗粒间能达到均一稳定的分散,悬浮粒子不会明显地沉降.凝胶注模成型所得坯体在2450℃和氩气氛下烧结可获得重结晶碳化硅高温材料,其体积密度为2.52g.cm-3,对应的抗弯强度为55.4MPa.
参考文献
| [1] | Omatete O O .Gelcasting a new ceramic forming process[J].Ceramic Bulletin,1991,70(10):1641-1649. |
| [2] | Janney M A;Omatete O O .Method for molding ceramics powders using a water-based gelcasting process[P].US:5145098,1992. |
| [3] | 杨金龙,谢志鹏,汤强,黄勇.α-Al2O3悬浮体的流变性及凝胶注模成型工艺的研究[J].硅酸盐学报,1998(01):41-46. |
| [4] | 司文捷 .直接凝固注模成型Si3N4及SiC陶瓷—基本原理及工艺过程[J].硅酸盐学报,1996,24(01):32-37. |
| [5] | YONG HUANG;LIGUO MA;QIANG TANG .Surface oxidation to improve water-based gelcasting of silicon nitride[J].Journal of Materials Science,2000(14):3519-3524. |
| [6] | Yang J L;Xie Z P;Ma J C.Study on gelcasting processing of high power rutile capacitor[M].Key Engineering Materials,1999:161-163. |
| [7] | L.Zhou;Y.Huang .Gelcasting of concentrated aqueous silicon carbide suspension[J].Journal of the European Ceramic Society,2000(1):85-90. |
| [8] | 陈宗淇;戴闽光.胶体化学[M].北京:高等教育出版社,1984:50-68. |
| [9] | 巴勒斯HA;赫顿 J H;瓦尔特斯 K;等,吴大诚,古大治.流变学引导[M].北京:中国石化出版社,1992:20-29. |
| [10] | 柏平舟;武洞明.再结晶碳化硅的工艺性能和烧结形状[J].国外耐火材料,1991(04):58-59. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%