采用醇-水法和柠檬酸络合法制备了CaO-ZrO2粉体,用XRD和TEM等手段对粉体的结构和形貌进行了表征.结果表明:醇-水法所得粉体的粒径在70nm左右,基本无团聚体存在;至800℃时,晶粒已经发育完好,与固相法相比,其合成温度降低了600℃左右;晶型结构为四方晶型,无单斜相存在.而柠檬酸络合法所得粉体中含有大量单斜相.将醇-水法所得粉体加入到BaTiO3中,进行烧结实验,与固相法合成的CaO-ZrO2粉体相比,它使BaTiO3的烧结温度降低了20℃左右.
参考文献
| [1] | Nguycn Q M .Ceramic Fuel Cell[J].Journal of the American Ceramic Society,1993,76(03):563-567. |
| [2] | 李懋强 .湿化学法合成陶瓷粉体的原理和方法[J].硅酸盐学报,1994,22(01):88-92. |
| [3] | Moon Y T;Park H K;Kin D K et al.Preparation of monodisperse and spherical zirconia powders by heating of alcohol-aqueous salt solutions[J].Journal of the American Ceramic Society,1995,78:2690-2694. |
| [4] | Li W;Gao L;Guo J K .Preparation of nanostructured ZrO2Y2O3[J].Nano-Structured Materials,1998(10):1043-1049. |
| [5] | 李蔚,高濂,郭景坤.醇-水溶液加热法制备纳米ZrO2粉体及相关过程的研究[J].无机材料学报,2000(01):16-20. |
| [6] | Okubo T.;Nagamoto H. .LOW-TEMPERATURE PREPARATION OF NANOSTRUCTURED ZIRCONIA AND YSZ BY SOL-GEL PROCESSING[J].Journal of Materials Science,1995(3):749-757. |
| [7] | Lin JD.;Duh JG. .COPRECIPITATION AND HYDROTHERMAL SYNTHESIS OF ULTRAFINE 5.5 MOL-PERCENT CEO2-2 MOL-PERCENT YO1.5-ZRO2 POWDERS[J].Journal of the American Ceramic Society,1997(1):92-98. |
| [8] | 高濂;乔海潮 .乳浊液法制备超细氧化锆粉体[J].无机材料学报,1994,9(02):217-220. |
| [9] | 郭伟巍 .BaO-TiO<,2>-Ln<,2>O<,3>系陶瓷材料的制备及性能研究[D].天津大学,2001. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%