采用DTA,XRD,SEM,TEM研究了MgO-Al2O3-SiO2-Li2O-R2O-F(R＝Na,K)玻璃系统晶化过程中的晶相与显微结构演变.结果表明,基础玻璃的分相自650℃开始;700℃以下,初期云母相出现;750℃β-锂辉石开始形成;850～950℃之间,随着Mg2+,K+,F-的扩散进入,β-锂辉石与玻璃相产生交代反应,以过渡相形式转变成云母类固溶体;在950℃以上;β-锂辉石不断转化为锂云母固溶体,云母晶体尺寸长大明显.
参考文献
| [1] | Grossman D G .Machinable glass-ceramics based on tetrasilic mica[J].Journal of the American Ceramic Society,1972,55(09):446-449. |
| [2] | Daniels W H;Moore R E .Crystallization of a tetrasilicic fluormica glass[J].Journal of the American Ceramic Society,1975,58(5-6):217-221. |
| [3] | 郑捷;吴勉学;诸培南 等.K2O-MgO-MgF2-SiO2系统固相反应与玻璃析晶相变反应的比较[J].无机材料学报,1988,3(01):1-8. |
| [4] | Baik DS.;Chun JSS.;No KS. .MECHANICAL PROPERTIES OF MICA GLASS-CERAMICS[J].Journal of the American Ceramic Society,1995(5):1217-1222. |
| [5] | Uno T;Kasuga T;Nakajima K .High strength mica-containing glass ceramics[J].Journal of the American Ceramic Society,1991,74(12):3139-3141. |
| [6] | 程慷果,万菊林,粱开明.云母微晶玻璃的热压强化和韧化[J].硅酸盐学报,1998(03):403-406. |
| [7] | 锂云母型可切削微晶玻璃[J].玻璃与搪瓷,1976(03):11. |
| [8] | 诸培南 .可切削微晶玻璃在仪表工业上的应用[J].仪表材料,1981,12(01):20-24. |
| [9] | 方平安;吴召平 .溶胶-增强凝胶涂层锂云母微晶玻璃[J].无机材料学报,2000,16(01):153-158. |
| [10] | 张何.合成云母[M].上海:上海科学技术出版社,1962:42-46. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%