Ti基金属复合材料是一种新型高温结构材料.本文利用放电等离子烧结技术,在温度1250℃、压力30MPa、真空度6Pa,保温时间10min条件下,制备了相对致密度较高的Ti/Al2O3复合材料.借助XRD,SEM,EDS等测试手段对该复合材料的物相组成、界面反应、微观结构以及致密度进行了观察与分析.结果表明:利用SPS技术制备Ti/Al2O3的复合材料,晶粒细小且分布均匀,结构致密、2相之间结合状态良好,相对致密度随材料中陶瓷相含量的增多而有所降低.Ti,Al2O32相之间无明显界面化学反应发生.
参考文献
| [1] | Huaxia J;Jones S .Characterization of the interaction between molten titanium alloy and Al2O3[J].Journal of Materials Science,1995,30:5617-5620. |
| [2] | Kclkar G P .Phase equilibria in the Ti-Al-O system at 945℃and analysis of Ti/Al2O3 reactions[J].Journal of the American Ceramic Society,1995,78(03):572-576. |
| [3] | Lu Hua;Bao C L .Study of the Ti/Al2O3 interface[J].Journal of Materials Science,1995,30:339-346. |
| [4] | A. M. KLIAUGA;M. FERRANTE .Interface compounds formed during the diffusion bonding of Al_(2)O_(3) to Ti[J].Journal of Materials Science,2000(17):4243-4249. |
| [5] | Gunther R;Klassen T .Advanced alumina composites reinforced with titanium-based alloys[J].Journal of the American Ceramic Society,2000,84(07):1509-1513. |
| [6] | 张东明,傅正义.放电等离子加压烧结（SPS）技术特点及应用[J].武汉工业大学学报,1999(06):15-17. |
| [7] | 葛志明.钛的二元系相图[M].北京:国防工业出版社,1977:6,48. |
| [8] | 李益民;郑子樵;吕维洁 .自蔓延高温反应合成Ti/Al2O3梯度功能材料[J].中南工业大学学报(自然科学版),1996,27(05):551-555. |
| [9] | 李克平;张同俊;李星国 等.激光加热在Al2O3/Ti系梯度功能材料制备过程中的作用及机理[J].激光技术,1997,21(03):174-178. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%