熔融分相法是制备负载型纳米TiO2光催化材料的新方法.该方法是以Na2O-B2O3-SiO2-TiO2系为研究对象,通过制备不同组成的样品,并进行X射线分析及显微分析,进一步研究了熔融分相法中玻璃分相与TiO2析晶的关系.结果表明:组成在玻璃分相区域的样品,有玻璃分相现象产生,TiO2晶体能够析出,而在未分相区域的组成,样品中没有产生玻璃分相,TiO2晶体不能析出;玻璃分相的结构影响了TiO2晶体的生长,相同热处理条件下,组成中硅含量越少,其玻璃分相程度越大,TiO2析晶越容易,TiO2的析晶尺寸越大.
参考文献
| [1] | Tada H;Tanaka M .Dependence of TiO2 photocatalytic activity upon its film thickness[J].Langmuir,1997,13:360-364. |
| [2] | 胡永茂,项金钟,李茂琼,方静华,张学清,吴兴惠.纳米TiO2的制备与表征[J].中国陶瓷,2002(05):19-21. |
| [3] | 符小荣,宋世庚,王学燕.纳米TiO2/Si薄膜的制备与光催化性能的研究[J].感光科学与光化学,1997(03):234. |
| [4] | Tennakone K;Kottegoda I R M .Photocatalytic mineralization of paraquat dissolved in water by TiO2 supported on polythene and poly propylene films[J].Journal of Photochemistry and Photobiology A:Chemistry,1996,93:79-81. |
| [5] | Subramania G.Visible frequency thim film photonic crystals from colloidal system of nanocrystalline titania and polystyren microspheres[J].Journal of the American Ceramic Society,2002(06):1383-1386. |
| [6] | 张文丽,赵英娜,张晓丽.熔融分相法制备TiO2光催化材料组成的选择[J].功能材料,2004(z1):2016-2018,2021. |
| [7] | 福格尔W;谢于深.玻璃化学[M].北京:中国轻工业出版社,1979:153-159. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%